Sintesis Katalis UiO-66/Al2O3-SiO2 Dan Aplikasinya Dalam Reaksi Esterifikasi Asam Oleat

Devi, Ni Ketut Rizkitha (2017) Sintesis Katalis UiO-66/Al2O3-SiO2 Dan Aplikasinya Dalam Reaksi Esterifikasi Asam Oleat. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1413100003-Undergraduate_Theses.pdf]
Preview
Text
1413100003-Undergraduate_Theses.pdf - Accepted Version

Download (3MB) | Preview

Abstract

Padatan UiO-66, UiO-66/Al2O3 (Zr/Al = 0,5) dan UiO-66/Al2O3-SiO2(variasi Si/Al = 1,2,4,6) telah berhasil disintesis dengan metode solvotermal pada suhu 120 °C selama 24 jam. Difraktogram menunjukkan bahwa padatan hasil sintesis menunjukkan puncak karakteristik pada 2θ= 7,3 dan 8,5°. Spektra FT-IR dari padatan hasil sintesis menunjukkan pita serapan pada bilangan gelombang yang sama yaitu 1400, 663 – 671, 1508 – 1581, 1656 – 1697 dan 3421 – 3446 cm-1 yang secara berturut – turut merupakan serapan dari gugus C-O streching , gugus Zr-O, gugus C=C aromatik, gugus C=O dan gugus –OH. Penambahan Al2O3 dan SiO2 tidak mengubah struktur dari UiO-66. Luas permukaan dari UiO-66 dan UiO-66/Al2O3-SiO2 (Si/Al = 1) secara berurutan adalah 466,997 dan 268,955 m2/g. Hasil uji aktivitas pada reaksi esterifikasi asam oleat menunjukkan bahwa dengan katalis UiO-66/Al2O3, UiO-66/Al2O3-SiO2 (rasio Si/Al = 1 dan 6) memiliki yield secara berturut – turut sebesar 7,61, 4,31, 4,94, 5,21%.
=================================================================
UiO-66, UiO-66/Al2O3 (Zr/Al = 0,5) dan UiO-66/Al2O3-SiO2 (with variation of Si/Al = 1,2,4,6) have been succesfully synthesized by solvothermal method at temperature 120 °C for 24h. The difractogram of materials had same characteristic peak with UiO-66 exhibited at 2θ= 7,4 and 8,5°. The FT-IR spectra had peak at 1400, 663-671, 1508-1581, 1656-1697 and 3421-3446 cm-1 which indicated the presence of C-O streching , Zr-O bonding, C=C aromatic, C=O bonding and –OH bonding respectively. The addition of Al2O3 and SiO2 were not change the structure of UiO-66. Surface area and pore volume of UiO-66 and UiO-66/Al2O3-SiO2 (Si/Al=1) were 466,997 and 268,955 m2/g, respectively. The catalyst activity for esterification oleic acid by UiO-66, UiO-66/Al2O3, UiO-66/Al2O3-SiO2 (the rasio Si/Al = 1 and 6) catalyst had yield of 7,61, 4,31, 4,94, 5,21 % respectively.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 547.27 Dev s
Uncontrolled Keywords: UiO-66, Al2O3, SiO2, metode solvotermal, aktivitas katalitik, solvothermal method, catalytic activity
Subjects: Q Science > QD Chemistry
Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Ni Ketut Rizkitha Devi
Date Deposited: 30 Oct 2017 07:01
Last Modified: 05 Mar 2019 07:36
URI: http://repository.its.ac.id/id/eprint/42990

Actions (login required)

View Item View Item