Karakterisasi Komposit Silicone Rubber Berpenguat Nanoselulosa Serat Tandan Kosong Kelapa Sawit dan Barium Heksaferrit untuk Aplikasi Penyerap Suara dan Penyerap Radar

Pratama, Rachmadhani Dian (2017) Karakterisasi Komposit Silicone Rubber Berpenguat Nanoselulosa Serat Tandan Kosong Kelapa Sawit dan Barium Heksaferrit untuk Aplikasi Penyerap Suara dan Penyerap Radar. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100063_Undergraduate_Theses.pdf - Published Version

Download (8MB) | Preview

Abstract

Komposit berpenguat nano filler merupakan satu material yang sedang dikembangkan. Salah satu aplikasinya dapat digunakan untuk menyerap suara. Sedangkan Barium Heksaferrit merupakan material yang memiliki sifat magnetik yang baik yang dapat menyerap gelombang elektromagnetik. Penelitian ini menggunakan silicone rubber berpori sebagai matriks, nanoselulosa dan barium heksaferrit sebagai filler. Variabel yang digunakan pada penelitian ini adalah penambahan Barium Heksaferrit dan tanpa penambahan Barium Heksaferrit. Tujuan dari penelitian ini adalah menganalisis pengaruh penambahan nanoselulosa dan Barium Heksaferrit terhadap nilai koefisien absorbsi suara dan nilai penyerapan gelombang elektromagnetik. Pengujian yang dilakukan dalam penelitian ini meliputi uji koefisien absorpsi suara, SEM, TEM, FTIR, densitas, dan uji VNA. Silicone Rubber berporous yang mengandung 6% nanoselulosa dan 10% BaM memiliki nilai α tertinggi 0.4762 pada frekuensi 4000 Hz dan nilai rugi refleksi tertinggi yaitu 23.016 dB pada frekuensi 8.39 GHz. =============================================================================================== Composite materials reinforced by nanofiller are now becoming one of the developed materials. It can be used as an acoustical material. Acoustical materials are often used as sound absorber. Meanwhile, barium hexaferrite is a material that has good magnetic properties which can absorb electromagnetic waves. This study used porous silicone rubber as the matrix, nanocellulose and barium hexaferrite as the filler. The variables used in this study were the addition of barium hexaferrite and without the addition of barium hexaferrite. The purpose of this research is to analyze the effect of nanocellulose and barium hexaferrit to the value of sound absorption coefficient and the value of electromagnetic wave absorption. Tests performed in this study were included sound absorption coefficient, SEM, TEM, FTIR, density and VNA test. Porous silicone rubber which containing 6% nanoselulosa and10% BaM has highest α value 0.4762 at frequency 4000 Hz and highest reflection loss value -23.016 dB at frequency 8.39 GHz.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Pra k-1
Uncontrolled Keywords: Tandan Kosong Kelapa Sawit, Nanoselulosa, Silicone Rubber Berpori, Barium Heksaferrit.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
T Technology > TP Chemical technology > TP1140 Polymers
T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: pratama Rachmadhani dian
Date Deposited: 14 Nov 2017 02:37
Last Modified: 05 Mar 2019 07:52
URI: http://repository.its.ac.id/id/eprint/43122

Actions (login required)

View Item View Item