Karakterisasi dan Proses Manufaktur Komposit Polypropylene Berpenguat Serat Dendrocalamus Asper untuk Ruang Mesin Otomotif

Basyarahil, Zulfa Ilham (2017) Karakterisasi dan Proses Manufaktur Komposit Polypropylene Berpenguat Serat Dendrocalamus Asper untuk Ruang Mesin Otomotif. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2713100066-Undergraduate_Theses.pdf]
Preview
Text
2713100066-Undergraduate_Theses.pdf - Published Version

Download (4MB) | Preview

Abstract

Kebisingan dapat mempengaruhi kenyamanan saat berkendara. Oleh karena itu pembuatan interior penumpang haruslah menggunakan material yang dapat mengabsorbsi suara. Sebelumnya, sudah diteliti mengenai komposit polypropylene berpenguat serat Dendrocalamus Asper dan penambahan MAPP sebagai coupling agent. Akan tetapi, penelitian sebelumnya masih dilakukan penelitian untuk prosesnya dan belum diaplikasikan untuk interior otomotif. Sehingga dibuatlah penelitian yang bertujuan untuk menganalisa material komposit polypropylene berpenguat serat Dendrocalamus Asper untuk diaplikasikan penyerapan suara bagian interior otomotif. Permasalahan yang dikaji untuk mengetahui nilai koefisien absorpsi suara, sifat fisik, serta sifat mekanik. Komposisi fraksi massa serat yang digunakan adalah 5%, 10%, 15% dan penambahan MAPP dengan komposisi sebesar 2 %. Tujuannya untuk mendapatkan nilai koefisien absorpsi suara terbaik serta sifat fisik dan mekanik yang paling baik. Metode yang digunakan berdasarkan standartd ASTM E 1050 untuk pengujian absorbs suara, ASTM D790 untuk pengujian flexural, dan ASTM D792 untuk pengujian densitas. Dari hasil pengujian dapat dilihat pada morfologi komposit polypropylene/MAPP/SB pori yang terbentuk semakin sedikit karena penambahan MAPP sebagai coupling agent untuk memperbaiki gaya adhesi antara serat dan matriks, sehingga poros yang dimiliki semakin kecil, ditunjukkan pula pada densitas penambahan SBB 10% memiliki nilai densitas yang terendah sehingga memiliki poros yang paling tinggi. Hasil Pengujian yang lain adalah nilai koefisien absorpsi suara, kekuatan lentur dan densitas tertinggi didapatkan pada fraksi massa 20% secara berturut turut 0.526 pada frekuensi 4000 Hz, 36.2861 Mpa, 1.224 gr/cm3. =======================================================================================================
Noise can affect comfort while driving. Therefore, the manufacture of passenger interiors must use materials that can absorb sound. Previously been studied about polypropylene with Dendrocalamus Asper fibre composite and addition of MAPP as coupling agent. However, previous research is still not done research for the process and has not been applied to automotive interiors. So, the research was made to analyze the composite material of polypropylene with Dendrocalamus Asper fibre for applied sound absorption of automotive interior parts. The problems studied to determine the value of sound absorption coefficient, physical properties, and mechanical properties. The composition of the fiber mass fraction used is 5%, 10%, 15% and the addition of MAPP with a composition of 2%. The goal is to get the best sound absorption coefficient value as well as the best physical and mechanical properties. The method used is based on the ASTM E 1050 standard for sound absorbs, ASTM D790 for flexural testing, and ASTM D792 for density testing. From the test results can be seen on the morphology of polypropylene / MAPP / SB pore composite that formed less and less because of the addition of MAPP as coupling agent to improve adhesion force between fiber and matrix, so that the porous owned is smaller, also shown at the density of additional 10% SBB has value lowest density so that it has the highest porous. Other test results are the value of sound absorption coefficient, bending strength and highest density obtained at 20% consecutive mass fraction 0.526 at frequency 4000 Hz, 36.2861 Mpa, 1.224 gr / cm3.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Sound Absorption Material, Interior, Serat Dendrocalamus Asper, Polypropylene, Sifat fisik, Sifat Mekanik
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TP Chemical technology > TP1140 Polymers
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Zulfa Ilham Basyarahil
Date Deposited: 22 Aug 2017 07:43
Last Modified: 05 Mar 2019 07:06
URI: http://repository.its.ac.id/id/eprint/43230

Actions (login required)

View Item View Item