Pengaruh Komposisi Paduan Dan Tebal Coating Pada Proses Flame Sprayed Coating Serbuk Zn-Al Terhadap Ketahanan Korosi Baja Karbon Di Lingkungan Air Laut

Cita, Igfar (2017) Pengaruh Komposisi Paduan Dan Tebal Coating Pada Proses Flame Sprayed Coating Serbuk Zn-Al Terhadap Ketahanan Korosi Baja Karbon Di Lingkungan Air Laut. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2713100024_Undergraduate_Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Proses korosi air laut berlangsung karena adanya unsur-unsur kimia, oksigen yang larut dan pengaruh bakteri. Korosi logam pada air laut mengikuti mekanisme pada elektrokimia dimana pada logam yang mengalami korosi terdapat tempat-tempat berupa anoda dan katoda. Salah satu metode perlindungan korosi adalah dengan thermal spray, yang pada penelitian ini menggunakan serbuk Zn-Al. Tujuan dari penelitian ini adalah untuk menganalisis pengaruh tebal coating dan komposisi paduan terhadap daya rekat coating Zn-Al dan perlindungan korosi pada baja. Substrat yang digunakan adalah baja AISI 1045 dan plat zinc allum. Variabel yang digunakan adalah tebal coating yang dilihat dari jumlah layer sebanyak 10, 12, dan 14 buah serta komposisi paduan 25%Zn-75%Al, 50%Zn-50%Al, dan 75%Zn-25%Al. Terdapat 7 pengujian yaitu surface roughness, salinitas, XRD, weight loss, DFT, pull off, dan mandrel. Dari hasil penelitian didapatkan sifat mekanik pada spesimen dengan komposisi paduan 50%Zn-50%Al dengan tebal 208 μm merupakan yang paling optimal, yang didukung juga dengan nilai laju korosinya. Nilai laju korosi dengan komposisi 50%Zn-50%Al merupakan yang paling kecil sehingga menunjukkan ketahanan korosi yang baik di air laut. Juga tidak terdapat senyawa FeCl2/FeCl3 yang ditemukan pada seluruh komposisi paduan material coating Zn-Al. ======================================================================================================================== The corrosion process in sea water takes place because of the chemical elements, dissolved oxygen and bacterial influences. Metal corrosion in seawater follows a mechanism in electrochemical where in corroded metals, there have anodes and cathodes. One method of corrosion protection is with thermal spray, which in this study using Zn-Al powder. The purpose of this study was to analyze the effect of coating thickness and alloy composition on Zn-Al coating adhesion and corrosion protection on steel. The substrates used are AISI 1045 steel and zinc allum plate. The variables used are coating thickness seen from 10, 12, and 14 layers, and alloy composition 25%Zn-75%Al, 50%Zn-50%Al, and 75%Zn-25%Al. There are 7 tests which are surface roughness, salinity, XRD, weight loss, DFT, pull off, and mandrel. Results showed that in 50%Zn-50%Al alloying composition, the optmum result from mechanical properties has been identified, which supported by value of corrosion rate. Corrosion rate in 50%Zn-50%Al alloying composition is the smallest than the other alloying composition, which means has good corrosion protection against sea water environment.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: korosi, coating, thermal spray, serbuk Zn-Al
Subjects: Q Science > Q Science (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
V Naval Science > V Naval Science (General)
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Igfar Cita .
Date Deposited: 28 Aug 2017 03:52
Last Modified: 28 Aug 2017 03:52
URI: http://repository.its.ac.id/id/eprint/43269

Actions (login required)

View Item View Item