Aminuddin, Aulia Ur Rahman (2017) Analisa Pengaruh Variasi Tegangan Terhadap Kualitas Sambungan Hasil pengelasan GTAW pada Material SA 266 Gr 2N with Clad Inconel 625 (Tube Sheet) dengan SA 213 TP 304 (Tube). Undergraduate thesis, Institu Teknologi Sepuluh Nopember.
Preview |
Text
2713100139-Undergraduate_Theses.pdf - Published Version Download (6MB) | Preview |
Abstract
HP heater adalah perlatan Heat Exchanger yang berfungsi untuk menaikkan temperatur feed water sesuai temperatur Boiler.Penelitian ini menggunakan material SA 213 TP 304 dan Inconnel 625 di pilih karena memiliki sifat ketahanan korosi yang tinggi.Kedua material ini di las menggunakan metode GTAW digunakan sebagai tube dan tube sheet pada HP heater,akan tetapi sering di jumpai di lapangan terjadi crack pada material ini.Kemudian peneliti melakukan Proses pengelasan menggunakan variasi heat input dengan tegangan 8v,10v,12v,14v,16v. Tujuan dari penelitian ini adalah untuk menganalisa pengaruh heat input (tegangan) terhadap sifat mekanik dan struktur mikro pada hasil pengelasan SA 266 GR2N Inconel 625(tube sheet) dengan SA 213 TP 304 (tube). Pada penelitian ini dilakuan Pengujian yaitu uji makro,uji mikro,uji XRD dan uji kekerasan.Didapatkan hasil pengujian bahwa daerah aman untuk di lakukan pengelasan pada parameter 8v dan 10v.Persipitat karbida ditemuka pada parameter 12v dan 14v.
======================================================================================================================== HP heater is a Heat Exchanger equipment that serves to raise the temperature of feed water according to Boiler temperature.This research uses SA material 213 TP 304 and Inconnel 625 are selected because they have high corrosion resistant properties. Both of these materials are welded using GTAW method which used as tube and tube sheet on HP heater, will often be encountered in crack issue on this material. Then you do Process Welding using variation of heat input with voltage 8v, 10v, 12v, 14v, 16v. The purpose of this research is to analyze the effect of heat input (voltage) on mechanical properties and micro structure on welding result SA 266 GR2N Inconel 625 (tube sheet) with SA 213 TP 304 (tube). In this trial, test, hardness test. Obtain the appropriate result for safety parameters at 8v and 10v parameters. Carbide recipients are featured on 12v and 14v parameters.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | SA 213 TP 304,Clad Inconel 625,GTAW, tegangan, struktur mikro, kekerasan. |
| Subjects: | T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Ur Rahman A Aulia |
| Date Deposited: | 07 Sep 2017 07:59 |
| Last Modified: | 05 Mar 2019 07:12 |
| URI: | http://repository.its.ac.id/id/eprint/43387 |
Actions (login required)
 |
View Item |