Gumilang, Rizal Andhika and Riswanda, Moch.Ilham (2017) Peningkatan Kinerja Membran Cellulose Acetate/Polyethylene Glycol (CA/PEG) dengan Penambahan Functionalized Carbon Nanotube (CNT). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2313100066-2313100103-Undergraduated_Thesis.pdf - Published Version Download (2MB) | Preview |
Abstract
Secara kesuluruhan 97% air yang ada di bumi merupakan air laut dan hanya 2% merupakan air tawar yang berbentuk es. Sedangkan hanya 1% air bersih yang ada di bumi digunakan untuk memenuhi kebutuhan hidup manusia dan industri. Air dibutuhkan manusia untuk kebutuhan air minum, air mandi dan air sanitasi. Sedangkan dalam industri sendiri air berperan penting dalam unit utilitas yaitu sebagai air umpan boiler, sebagai pembangkit lsitrik ataupun sebagai pendingin pada heat exchanger. Oleh karena itu dibutuhkan suatu sistem pengolahan air yang baik dalam rangka untuk memenuhi kebutuhan hidup manusia ataupun dalam pemenuhan kebutuhan utilitas dalam industri. Desalinasi merupakan proses pemisahan untuk mengurangi kandungan garam atau zat terlarut hingga konsentrasi tertentu sehingga dapat dikonsumsi. Oleh karena itu, pada penelitian ini akan dilakukan sintesa membran CA/PEG dengan penambahan CNT 0.0125, 0.025, 0.0375, 0.05 gram yang telah difungsionalisasi wet dan dry method. Hasil fluks yang didadapatkan CPCU 0, CPCU 1, CPCU 2, CPCU 3, CPCU 4 berturut turut 333.33 L/m2.hr, 800 L/m2.hr, 906.67 L/m2.hr, 1093.33 L/m2.hr, 1233.33 L/m2.hr. Dan untuk Salt rejection CPCU 0, CPCU 1, CPCU 2, CPCU 3, CPCU 4 berturut turut 44.511%, 46.172%, 48.536%, 49.303%, 48.600%. Dari penelitian didapatkan membran terbaik yaitu CPCU 4 yaitu CA/PEG dengan penambahan CNT 0.05 gram.
============================================================
Over 97% of the earth’s water is the ocean water and only 2% is fresh water that is stored as ice cap. That leaves only 1% of the earth’s water is fresh water that available for human daily needs and industry needed. People needs water for drinking water, bathing water and water sanitation. While in industry, water acts as boiler feed water, power plants, and cooler at heat exchanger. Therefore needed the water treatment processes for supply human daily needs and supply utility needs in industry. Desalination is a separation process to decrease salt and other solute until certain concentrations so that will be consumed. Therefore in this research will be made CA/PEG membrane with added functionalized CNT of 0.0125, 0.025, 0.0375, 0.05 grams that functionalized with wet and dry method. The flux of CPCU 0, CPCU 1, CPCU 2, CPCU 3, CPCU 4 respectively 333.33 L/m2.hr, 800 L/m2.hr, 906.67 L/m2.hr, 1093.33 L/m2.hr, 1233.33 L/m2.hr. And Salt rejection CPCU 0, CPCU 1, CPCU 2, CPCU 3, CPCU 4 respectively 44.511%, 46.172%, 48.536%, 49.303%, 48.600%. From the research the best membrane is CA/PEG with added 0.05 grams CNT.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | membran, fungsionalisasi, salt rejection |
| Subjects: | T Technology > TP Chemical technology > TP1140 Polymers T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles. |
| Divisions: | Faculty of Industrial Technology > Chemical Engineering > 24201-(S1) Undergraduate Thesis |
| Depositing User: | Rizal Andhika Gumilang |
| Date Deposited: | 26 Sep 2017 01:56 |
| Last Modified: | 06 Mar 2019 03:38 |
| URI: | http://repository.its.ac.id/id/eprint/44092 |
Actions (login required)
 |
View Item |