Analisis Pengaruh Variasi Arus dan Kecepatan Pengelasan Tungsten Inert Gas terhadap Struktur Mikro dan Kekerasan Baja Tahan Karat SS304

Maula, Ihsan (2017) Analisis Pengaruh Variasi Arus dan Kecepatan Pengelasan Tungsten Inert Gas terhadap Struktur Mikro dan Kekerasan Baja Tahan Karat SS304. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2713100018-Undergraduated_Theses.pdf] Text
2713100018-Undergraduated_Theses.pdf
Restricted to Repository staff only

Download (11MB) | Request a copy

Abstract

Salah satu metode yang digunakan untuk menyambungkan baja tahan karat austenitik SS304 adalah las tungsten inert gas (TIG). Parameter pengelasan pada baja tahan karat austenitik dapat mempengaruhi morfologi, struktur mikro, nilai kekuatan tarik, bahkan mengakibatkan keretakan pada daerah las akibat heat input yang diberikan. Dibutuhkan heat input yang sesuai agar tidak mengurangi kualitas baja tahan karat SS304 salah satunya dengan cara menentukan arus dan keccepatan pengelasan. Penelitian kali ini bertujuan untuk menganalisis pengaruh variasi arus dan kecepatan pengelasan terhadap struktur mikro dan kekerasan serta menganalisis hubungan antara struktur mikro dan kekerasan hasil las. Pada penelitian ini dilakukan pengelasan TIG dengan variasi arus 80, 90, 100, dan 110 A serta kecapatan pengelasan 12, 18, dan 24 cm/min pada baja tahan karat SS304 berbentuk plat dengan tebal 5 mm. Setelah dilakukan pengelasan dilakukan pengujian makro, metalografi, XRD, serta kekerasan. Dari hasil pengujian makro dapat diamati perbedaan dari daerah weld metal dan base metal. Dari hasil pengujian XRD diketahui bahwa tidak adanya cacat las yang biasanya terjadi pada pengelasan baja tahan karat berupa presipitasi karbida atau fasa sigma. Pada pengamatan struktur mikro diketahui bahwa terdapat fasa austenit dan ferit pada tiga daerah las yang berbeda. Dari pengujian kekerasan didapatkan bahwa nilai kekerasan paling tinggi terdapat pada spesimen dengan parameter kecepatan pengelasan 24 cm/min dan arus 100 ampere. Kenaikan jumlah ferit dan penurunan ukuran butir pada struktur mikro menyebabkan kenaikan nilai kekerasan pada spesimen pengelasan.
===========================================================================================
One method used to join SS304 austenitic stainless steel is tungten inert gas welding (TIG). The welding parameters in austenitic stainless steels may affect morphology, microstructure, tensile strength values, even resulting in cracks in the weld area due to given heat input. It takes the appropriate heat input so as not to reduce the quality of SS304 stainless steel one of them by determining the current and speed of welding. This research aims to analyze the influence of current variation and speed of welding to micro structure and hardness as well as to analyze the relationship between micro structure and hardness of weld result. In this study TIG welding with variations of current 80, 90, 100, and 110 A as well as welding density 12, 18, and 24 cm / min on SS304 stainless steel plate shaped with a thickness of 5 mm. After welding done macro testing, metallography, XRD, and hardness. From the macro test results can be observed differences from the weld metal and base metal areas. From the results of XRD testing it is known that the absence of welding defects that usually occur in stainless steel welding in the form of carbide or sigma phase precipitation. In observation of microstructure it is known that there are austenite and ferrite phases in three different welding areas. From hardness testing it was found that the highest hardness value was found in specimens with welding speed parameters of 24 cm / min and 100 ampere current. An increase in the amount of ferrite and decreasing grain size on the microstructure leads to an increase in the hardness value of the welded specimen.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: SS304, TIG, arus, kecepatan pengelasan, struktur mikro, kekerasan, current, travel speed, microstructure, hardness
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TS Manufactures
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Ihsan Maula
Date Deposited: 06 Oct 2017 03:10