Efektiviitas Metode Surface Coating dan Blending untuk Penambahan Titanium Dioxide pada Membran Cellulose Acetate/Polyethylene Glycol (CA/PEG)

Zaim, Ryanda Luthfi and Muqni, Wahyuni Eka (2017) Efektiviitas Metode Surface Coating dan Blending untuk Penambahan Titanium Dioxide pada Membran Cellulose Acetate/Polyethylene Glycol (CA/PEG). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2313100005-2313100071-Undergraduate_Theses.pdf
Restricted to Repository staff only

Download (5MB) | Request a copy

Abstract

Kebutuhan akan air bersih terus meningkat. Oleh karena itu, perlu dicari alternatif untuk mendapatkan air bersih. Salah satu caranya adalah proses desalinasi dengan menggunakan membran. Membran cellulose acetate/polyethylene glycol (CA/PEG) merupakan salah satu jenis membran yang bisa digunakan untuk proses desalinasi. Beberapa penelitian tentang pembuatan membran CA/PEG telah dilakukan, tetapi belum menghasilkan membran dengan kinerja yang bagus. Penelitian ini dilakukan untuk melihat efektivitas penggunaan metode surface coating dan blending terhadap kinerja membran. Dalam penelitian ini dilakukan penambahan TiO2 dengan beberapa komposisi (0; 0.25; 0.5; 0.75; 1; 1.25; 1.5) g/L solvent untuk masing-masing metode. Hasil penelitian menunjukkan bahwa hidrofilisitas dan salt rejection meningkat dengan penambahan TiO2 hingga 1 g/L solvent untuk metode surface coating. Sedangkan untuk metode blending, meningkat hingga penambahan TiO2 0.5 g/L solvent dan menurun dengan semakin besar jumlah TiO2 yang ditambahkan. Berdasarkan analisa yang dilakukan, diperoleh membran dengan kinerja terbaik dengan metode blending yaitu pada penambahan TiO2 0.5 g/L solvent dengan salt rejection 47% dan water flux sebesar 98 L/m2.h =============================================================================================== The need for clean water continues to increase. Therefore, it is necessary to find an alternative for the get of clean water. One way is desalination process using membrane. Cellulose Acetate/Polyethylene Glycol (CA / PEG) membrane is one type of membrane that can be used for desalination process. Several studies on the manufacture of CA / PEG membranes have been performed, but have not yet produced a good performance membrane. This study was conducted to look at the effectiveness of using the method of surface coating and blending the performance of the membrane. This study using some compositions of TiO2 (0; 0.25; 0.5; 0.75; 1; 1.25; 1.5) g/L solvent for each method. The results showed that the hydrophilicity and salt rejection increases with the addition of TiO2 up to 1 g/L solvent for surface coating method. Blending method, hydrophilicity and salt rejection increases until the addition of TiO2 0.5 g/L solvent and decreases with further addition of TiO2. Based on the analysis, the best performance is obtained by adding TiO2 0.5 g/L solvent with salt rejection 47% and water flux 98 L/h.m2.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: CA, desalinasi,, membran PEG, TiO2
Subjects: T Technology > T Technology (General)
T Technology > TP Chemical technology
T Technology > TP Chemical technology > TP1140 Polymers
Divisions: Faculty of Industrial Technology > Chemical Engineering > (S1) Undergraduate Theses
Depositing User: Wahyuni Eka Muqni
Date Deposited: 30 Nov 2017 02:09
Last Modified: 30 Nov 2017 02:28
URI: http://repository.its.ac.id/id/eprint/44196

Actions (login required)

View Item View Item