Pembuatan Dietil Eter dengan Katalis Berbasis γ-Al2O3 Dipromote dengan Logam Cr dan Co dalam Reaktor Fixed Bed

Reza, Mukhamad Afif Deny and Novenia, Teresia Dyah (2017) Pembuatan Dietil Eter dengan Katalis Berbasis γ-Al2O3 Dipromote dengan Logam Cr dan Co dalam Reaktor Fixed Bed. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2315105005-2315105029-Undergraduate-Theses.pdf - Published Version

Download (3MB) | Preview

Abstract

Menipisnya sumber daya energi dikarenakan meningkatnya penggunaan bahan bakar dari tahun ke tahun, sehingga diperlukan upaya untuk mencari energi alternatif yang ramah lingkungan. Dietil eter merupakan salah satu bahan bakar alternatif yang bisa menggantikan bahan bakar fosil. Dietil eter dibuat melalui proses dehidrasi senyawa etanol dan menggunakan katalis alumina. Penelitian ini bertujuan untuk mempelajari cara pembuatan katalis Cr-Co/γ-Al2O3 dengan menggunakan metode incipient wetness impregnation, Mempelajari pengaruh perbandingan logam Cr-Co yang di impregnasikan pada γ-Al2O3 terhadap aktifitas katalis, dan mencari temperatur yang paling baik untuk proses produksi DiEtil Eter dari etanol 96%. Tahap pertama penelitian ini adalah proses preparasi nanokatalis γ-Al2O3 dengan metode presipitasi. γ-Al2O3 yang dihasilkan dilakukan karakterisasi XRD dan BET. Tahap kedua adalah melakukan impregnasi katalis γ-Al2O3 dengan logam Cr dan Co pada loading 10% dengan perbandingan logam Cr-Co (1:1 ; 1:2 dan 2:1). Kemudian katalis Cr-Co/γ-Al2O3 dilakukan karakterisasi XRD, BET dan SEM-EDX. Tahap ketiga adalah uji aktifitas katalis Cr-Co/γ-Al2O3 pada proses produksi Dietil Eter melalui dehidrasi etanol. Proses dehidrasi dilakukan pada reaktor fixedbed dengan temperatur operasi 125-225ºC, produk reaksi kemudian akan dilakukan analisa GC. Dari penelitian didapatkan hasil karakterisasi XRD dengan ukuran 17,9001 nm dan karakterisasi BET dengan luas permukaan 162,840 m2/g dan volume pori sebesar 0,3178 cc/g. Hasil analisa GC ditunjukkan bahwa konversi tertinggi pada impregnasi logam 2:1 pada suhu 225ºC sebesar 23,48% dan yield DEE tertinggi adalah 1,32% pada impregnasi logam 2:1 pada suhu 125 ºC. ================================================================= The depletion of energy resource is due to the increasing use of fuels from year to year, so it takes effort to find alternative energy that is environmentally friendly. Diethyl Eter is one of the alternative fuels that can replace fossil fuels. Diethyl Eter is prepared by dehydration ethanol and using alumina catalyst. Alumina, especially γ-Al2O3 is widely used as a catalyst and support catalyst. The objective of this research is to study how to manufacture Cr-Co/γ-Al2O3 catalyst by using incipient wetness impregnation method, to study the effects of Cr – Co metals which are impregnated on γ-Al2O3 to activity catalyst, and to find the best temperature for producing Diethyl Eter from ethanol 96%. The first stage of this research was the preparation process for γ-Al2O3 nanocatalyst with precipitation method. γ-Al2O3 product, to be characterized by XRD and BET. The second stage was to impregnate the γ-Al2O3 catalyst with Cr and Co metals at 10% loading by the ratio metals of Cr-Co (1:1 ; 1:2 and 2:1). Then Cr-Co/γ-Al2O3 was characterized by XRD, BET, and SEM-EDX. The third stage was the activity test of Cr-Co/γ-Al2O3 catalyst for the production process Diethyl Eter from dehydration ethanol. The dehydration process was done in the fixed bed reactor with temperature condition 125-225ºC the reaction product and will be analyzed by GC. The research showed that the result for XRD characterization with size is 17,9001 nm and BET characterization with surface area is 162,840 m2/g and pore volume is 0,3178 cc/g. The result from GC showed that the highest conversion in the metal impregnation 2:1 at temperature 225 ºC is 23,48% and the highest of yield DEE is 1,32% at metal impregnation 2:1 at temperatur 125 ºC.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Dietil eter, Etanol, Nanokatalis Cr-Co/γ-Al2O3
Subjects: Q Science > QD Chemistry
Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions: Faculty of Industrial Technology > Chemical Engineering > 24201-(S1) Undergraduate Thesis
Depositing User: Mukhamad Afif Deny Reza
Date Deposited: 29 Nov 2017 01:11
Last Modified: 06 Mar 2019 04:39
URI: http://repository.its.ac.id/id/eprint/44317

Actions (login required)

View Item View Item