Identifikasi Penyebaran Zona Korosi dan Estimasi Laju Korosinya serta Tempat Pemasangan Anoda untuk Proteksi Katodik pada Lapangan Unit 7 & 8 PT. IPMOMI Menggunakan Metode Resistivitas 2D konfigurasi Wenner Alpha

Syahwirawan, Yuri (2017) Identifikasi Penyebaran Zona Korosi dan Estimasi Laju Korosinya serta Tempat Pemasangan Anoda untuk Proteksi Katodik pada Lapangan Unit 7 & 8 PT. IPMOMI Menggunakan Metode Resistivitas 2D konfigurasi Wenner Alpha. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
3713100701-Undergraduate_Theses.pdf
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Korosi merupakan proses perusakan pada permukaan logam akibat pengaruh lingkungan yang korosif. Pada PT. IPMOMI terdapat jaringan pipa transmisi yang dapat mengalami korosi dan mengakibatkan kerugian besar bagi perusahaan. Lokasi pemasangan jaringan pipa tersebut merupakan tanah reklamasi (tanah urukan) yang ditimbun di bibir pantai sehingga pengaruh air laut menjadikan potensi korosi sangat tinggi. Untuk mengetahui penyebaran lingkungan korosi dan tempat pemasangan anoda yang tepat untuk proteksi katodik maka dilakukan penelitian geolistrik menggunakan metode resistivitas 2D dengan konfigurasi Wenner Alpha. Hasil pengukuran didapatkan pada kedalaman 0 meter sampai 4 meter didominasi oleh zona korosivitas sangat rendah dengan nilai resistivitas lebih dari 50 Ωm yang memiliki laju korosi kurang dari 3,49 mil/th. Pada kedalaman lebih dari 4 meter didominasi oleh zona korosivitas sangat tinggi dengan nilai resistivitas dibawah 7 Ωm yang memiliki laju korosi lebih dari 5,04 mil/th. Lokasi pemasangan anoda adalah pada nilai resistivitas 8 Ωm hingga 20 Ωm yaitu pada lintasan 2 diantara bentangan 10 meter sampai 20 meter di kedalaman ±3 meter, pada lintasan 3 diantara bentangan 20 meter sampai 28 meter di kedalaman ± 3 meter, dan pada lintasan 5 diantara bentangan 20 meter sampai 25 meter dikedalaman ±3 meter. ============================================================================================= Corrosion is a process of destruction on metal surfaces due to corrosive environmental influences. At PT. IPMOMI there is a transmission pipe line that can experience corrosion and theft of losses for the company. The location of the pipe line installation is reclaimed soil which is dumped on the shor e so that it affects the sea water making the corrosion potential ve ry high. To find out the potential of corrosion environment and anode mounting place for cathodic protection, geoelectric res earch was done by resistivity 2D method with Wenner Alpha configuration. Measurement results at depths of 0 meters to 4 meters are dominated by very low corrosivity zones with resistivity values greater than 50 Ωm having corrosion rates of less than 3.49 mil s/yr . At a depth of more than 4 meters is dominated by a very high corrosivity zone with a resistivity value below 7 Ωm having a corrosion rate of more than 5.04 mil s/yr . The location of anode mounting is at res istivity of 8 Ωm to 20 Ωm on line 2 between 10 meters to 20 meters in depth of ± 3 meters, on line 3 between the stretch of 20 meters to 28 meters at depth of ± 3 meters, and on line 5 between 20 meters to 25 meters in depth ± 3 meters.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Anoda, Korosi, Laju korosi, Resistivitas 2D, Wenner alpha, Anode, Corrosion, Corrosion rate, 2D Resistivity
Subjects: Q Science > QE Geology > QE601 Geology, Structural
T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions: Faculty of Civil Engineering and Planning > Geophysics Engineering > (S1) Undergraduate Theses
Depositing User: Yuri Syahwirawan
Date Deposited: 12 Oct 2017 07:09
Last Modified: 03 Jan 2018 04:49
URI: http://repository.its.ac.id/id/eprint/44687

Actions (login required)

View Item View Item