Pemanfaatan Fly Ash dan Bottom Ash dari PLTU Suralaya Banten untuk pembuatan GEOPAV

Thahir, Zainal Abidin (2017) Pemanfaatan Fly Ash dan Bottom Ash dari PLTU Suralaya Banten untuk pembuatan GEOPAV. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
3115105005-Undergraduated_Theses.pdf
Restricted to Repository staff only

Download (3MB) | Request a copy

Abstract

Berdasarkan database oleh Badan Geologi Departemen Energi dan Sumber daya mineral (ESDM) Sumber daya batu bara di Indonesia mencapai 65,4 Miliar Ton, salah satu cara untuk memanfaatkan batu bara tersebut adalah melalui pembangkit listrik tenaga uap (PLTU).Limbah batu bara didapatkan dari PLTU Suralaya Banten.PLTU Suralaya sebagai salah satu anak perusahaan dari PLN dan IPP yang menghasilkan limbah batu bara sebesar 2,7 juta ton/tahun dan bisa terus bertambah hingga 11,2 juta ton/tahun pada tahun 2027). Sejauh ini penanganan limbah batu bara masih dalam bentuk penimbunan.Hal ini dirasa tidak tepat dikarenakan penimbunan akan terus bertambah sehingga kebutuhan lahan pun semakin besar. Oleh karena itu pada penelitian ini diharapkan bisa membantu mengatasi permasalahan pengolahan limbah batu bara khususnya dari PLTU Suralaya banten.Salah satu cara pemanfaatan dan pengolahan limbah batu bara Fly Ash dan Bottom Ash (FABA) yaitu dengan memproduksi menjadi Paving Block Geopolimer atau biasa disebut dengan GEOPAV. Perbandingan komposisi yang digunakan antara lain pasta dengan agregat adalah 30:70.Agregat terdiri dari pasir, batu pecah, dan abu batu ditambah bottom ash. Variasi komposisi bottom ash menggantikan peran pasir dan abu batu sebesar 50%.Pasta terdiri Fly ash dn larutan alkali , larutan alkali dari Na2SiO3 dan NaOH 8M adalah 1:1. Berdasarkan perhitungan analisa biaya GEOPAV perbuah sebesar Rp. 900,-. Margin Harga Produksi GEOPAV (HPP) dengan Harga Jual Produsen lokal sebesar 62%. Didapatkan hasil bahwa komposisi GEOPAV menggantikan peran pasir dan abu batu sebesar 50% memiliki kualitas baik. Berdasarkan SNI 03-0691-1996 tentang paving block dikategorikan paving mutu kelas A.Nilai kuat tekan rata-rata besar 43,37 MPa, dalam nilai ketahanan aus rata-rata sebesar 0,060 mm/menit, dan dalam nilai resapan air rata-rata sebesar 12,06%. =============================================================================================== Based on the data from Geological Agency of the Department of Energy and Mineral Resources (ESDM) there are approximately 65.4 Billion Ton of Coal resources in Indonesia. One way to utilize the coal is by using it as fuel for coal-fired power plant (PLTU). Coal waste was obtained from PLTU Suralaya Banten.Suralaya Power Plant is one of subsidiaries of PLN and IPP that produces coal waste of 2.7 million tons per year and can continues to grow up to 11.2 million tons / year on Year 2027). Until now there is only few of effort to reduce the amount of coal waste. This is be a big problem because the waste accumulation needs of more land continuous. Therefore, this research is expected to solve the problem of coal waste, Reduction especially from Suralaya power plant Banten.One solution for this problem is using the waste materials such as Fly Ash and Bottom Ash (FABA) to produce Paving Block Geopolymer or commonly referred as GEOPAV. The mix composition consist of 30% paste and 70% aggregate. Aggregates consist of sand, crushed stone, and Coal ash plus bottom ash. Variation composition of Bottom ash replaces the role of sand and coal ash by 50%.The paste made of iv Fly ash and soluble alkali. The soluble alkali consist of Na2SiO3 and NaOH 8M with the ratio of 1: 1. Based on the calculation, the cost of GEOPAV is Rp. 1,049, -. The cost difference of GEOPAV and Local insdustrial paving is 62%. The composition of GEOPAV that use bottom ash to replace 50% of sand and coal ash has good quality. Based on SNI 03-0691-1996 about paving block GEOPAV categorized as class A paving.The average compressive strength is 43,37 MPa, wear resistance value is 0.060 mm / min, and water absorption rate is 12.06%.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: paving, geopolymer, fly ash, bottom ash, the analysis of costs, quality of paving blocks.
Subjects: Q Science > QD Chemistry > Polymerization
T Technology > TA Engineering (General). Civil engineering (General) > TA681 Concrete construction
T Technology > TP Chemical technology > TP1140 Polymers
Divisions: Faculty of Civil Engineering and Planning > Civil Engineering > (S1) Undergraduate Theses
Depositing User: Zainal Abidin Thahir
Date Deposited: 24 Nov 2017 03:22
Last Modified: 24 Nov 2017 03:22
URI: http://repository.its.ac.id/id/eprint/44709

Actions (login required)

View Item View Item