Puspitorini, Aulia (2017) Analisis Sisa Umur Kelelahan Pada UW-Pro Platform Menggunakan Metode Cummulative Damage Dan Fracture Mechanics. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
4313100094-Undergraduate_Theses.pdf - Published Version Download (3MB) | Preview |
Abstract
Dalam mendesain suatu struktur atau anjungan lepas pantai didasarkan dari kebutuhan lama beroperasinya. Sehingga tiap anjungan atau struktur lepas pantai memiliki umur kelelahan yang berbeda-beda. Perhitungan umur kelelahan sendiri bisa diketahui dengan dua metode yaitu cummulative damage dan fracture mechanics. Pada penelitian ini akan menganalisa umur kelelahan struktur menggunakan perbandingan dua metode tersebut. Struktur yang dijadikan sebagai objek penelitian adalah UW-Pro Platform milik Pertamina Hulu Energi Offshore North West Java. Struktur akan dianalisa secara global menggunakan metode cummulative damage dan joint yang memiliki fatigue life yang pendek akan dianalisa secara lokal. Untuk perhitungan fracture mechanics dimulai dengan menentukan nilai Stress Intensity Factor (SIF) dan besarnya perambatan retak sehingga umur kelelahan dari struktur bisa diketahui. Hasil dari analisa menggunakan metode cummulative damage adalah sebesar 131 tahun, lalu menggunakan metode fracture mechanics adalah sebesar 98 tahun. Perbedaan hasil dari kedua metode tersebut adalah sebesar 33 tahun, jadi disimpulkan bahwa crack atau retak dapat mengurangi umur kelelahan secara signifikan.
=================================================================
In designing an offshore structure or a platform based on how long the operation is. So each platform or offshore structure has a different fatigue life. Analysis of fatigue life can be known by two methods of cummulative damage and fracture mechanics. In this study will analyze the fatigue life of the structure using a comparison between two methods. The structure used as research object is UW-Pro Platform owned by Pertamina Hulu Energi Offshore North West Java. Structures will be analyzed globally using cummulative damage and joint that have short fatigue lif e will be analyzed locally. For the analysis of fracture mechanics begins by determining the value of Stress Intensity Factor (SIF) and the magnitude of the crack propagation so that fatigue life of the structure can be known. Fatigue life results of the analysis using cummulative damage method is 131 years,then using fracture mechanics is 98 years. The differences result between two method is 33 years,so the conclusion is a crack can reduced fatigue life significantly.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | cummulative damage, fracture mechanic, fatigue life, stress intensity factor. |
| Subjects: | T Technology > TC Hydraulic engineering. Ocean engineering > TC1680 Offshore structures |
| Divisions: | Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis |
| Depositing User: | Aulia Puspitorini . |
| Date Deposited: | 24 Nov 2017 04:03 |
| Last Modified: | 06 Mar 2019 07:01 |
| URI: | http://repository.its.ac.id/id/eprint/44767 |
Actions (login required)
 |
View Item |