Analisis Pengaruh Suhu Preheating Pada Pengelasan Baja Karbon Sedang (ASTM A53) Terhadap Sifat Mekanik dan Ketahanan Korosi Weld Joint Pada Lingkungan Laut

Palgunadhi, Hasri (2017) Analisis Pengaruh Suhu Preheating Pada Pengelasan Baja Karbon Sedang (ASTM A53) Terhadap Sifat Mekanik dan Ketahanan Korosi Weld Joint Pada Lingkungan Laut. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
4313100002-Undergraduate-Theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Pengelasan adalah proses penyambungan logam dengan memanfaatkan energi panas. Pengelasan yang memanfaatkan energi panas ini mengakibatkan terjadinya siklus thermal. Karena hal tersebut maka menyebabkan perubahan-perubahan sifat metalurgi yang rumit, deformasi dan tegangan thermal. Siklus thermal adalah proses pemanasan dan pendinginan di daerah lasan (weld joint). Lama waktu siklus thermal dalam proses pengelasan sangat mempengaruhi kualitas hasil lasan. Banyak upaya dilakukan untuk mengendalikan pendinginan ataupun pemanasan pada logam yang dilas. Salah Satu cara untuk mengendalikan siklus thermal tersebut adalah dengan perlakuan panas sebelum proses pengelasan. Pada tugas akhir penelitian menggunakan material jenis baja karbon sedang (ASTM A53), pada penelitian ini akan dilakukan analisis pengaruh suhu pemanasan mula (preheating) terhadap sifat mekanik dan ketahanan korosi sambungan las (weld joint) pada lingkungan laut. Pemanasan mula pada penelitian tugas akhir ini dengan suhu 100⁰C, 200⁰C dan 300⁰C. Metode pengelasan yang digunakan adalah Shielded Metal Arc Welding (SMAW). Setelah dilakukan pengelasan spesimen selanjutnya diuji korosi menggunakan sel tiga elektroda, uji kekerasan dengan metode vickers, uji kekuatan dengan uji tarik dan uji metalografi untuk mengetahui bentuk struktur material. Setelah pengujian dilakukan, didapatkan perlakuan variasi 200⁰C yang memberikan hasil terbaik. ================================================================== Welding is the process of joining metals by utilizing heat energy. Welding utilizing heat energy resulted in a thermal cycle. Because of this it causes changes in metallurgical properties are complicated, deformation and thermal stress. Thermal cycle is the process of heating and cooling in the weld joint zone. The time of thermal cycle and welding process very influential to quality of weld joint. There are many ways to control the cooling or heating on the metal being welded. One of many ways to control thermal cycle is phe heat weld threatment. On this final exam research, use medium carbon steel material (ASTM A53). In this research will be analyzed the influence of preheating temperature on mechanical properties and corrosion resistance on marine. The temperature of preheating on this research are consist of 100⁰C, 200⁰C and 300⁰C. The welding method in this research is shielded metal arc welding (SMAW). After welding process of specimen finish, then our spesismen tested for corrosion resistance use potensiostat autolab, hardness test use vickers method, tensile strength test and metalographi test to know the shape of material structure. After the material test was done, the preheat treatment of 200⁰C variation gave the best result.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Preheating, Shielded Metal Arc Welding (SMAW), ASTM A53
Subjects: T Technology > TC Hydraulic engineering. Ocean engineering > TC1680 Offshore structures
V Naval Science > V Naval Science (General)
Divisions: Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User: Hasri Palgunadhi
Date Deposited: 16 Oct 2017 04:37
Last Modified: 08 Mar 2019 03:58
URI: http://repository.its.ac.id/id/eprint/45602

Actions (login required)

View Item View Item