Analisa Teknis Bahan Komposit Dari Serat Alami Ampas Tebu Untuk Bahan Alternatif Pembuatan Kulit Kapal

Pujiati, Retno (2017) Analisa Teknis Bahan Komposit Dari Serat Alami Ampas Tebu Untuk Bahan Alternatif Pembuatan Kulit Kapal. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
4212100105-undergraduate_theses.pdf - Published Version

Download (1MB) | Preview

Abstract

Tujuan penelitian adalah mengetahui kekuatan tarik dan impact komposit serat tebu. Manfaat penelitian ini adalah dapat menjadi acuan untuk penelitian berikutnya lebih pada pengembangan komposit khususnya yang menggunakan serat tebu. Dan dibandingkan dengan nilai standar yang diisyaratkan oleh BKI,yaitu kuat Tarik sebesar 98 N/mm2 dan modulus elastisitas 6,86 x 103 N/mm2 Komposit dibuat dengan metode hand lay up, bahan yang digunakan adalah resin polyester merk BQTN, serat tebu dengan dan dengan perbandingan serat dan resin yaitu 55%:45%, 60%:40%, 65%:35%. Serta dengan variasi kadar air serat yaitu 3%, 6%, 10%. Hasil pengujian menunjukan kekuatan tarik komposit serat tebu dengan fraksi volume 65% memiliki nilai kuat Tarik dan impact lebih besar yaitu 20 N/mm2, daripada yang lainnya. Komposit serat tebu dengan kadar air 10% memiliki nilai kuat Tarik dan impak paling tinggi yaitu 20 N/mm2, daripada komposit dengan kadar air 6% dan 3%. Nilai kuat Tarik semua specimen masih belum memenuhi standar BKI. Ini karena komposit yang dibuat hanya 1 layer, kemungkinan jika komposit dibuat dengan beberapa layer akan dapat memenuhi nilai standar BKI. ===================================================================================== The purpose of this research is to know tensile strength and impact of sugarcane fiber. The benefits of this research is to become a reference for further research on the development of composites, especially those using sugarcane fiber. And compared to the standard values implied by BKI, ie Strength Drag of 98 N / mm2 and the modulus of elasticity of 6.86 x 103 N / mm2 The composite is made by hand lay up method, the material used is BQTN polyester resin, sugar cane with and with fiber and resin ratio of 55%: 45%, 60%: 40%, 65%: 35%. As well as variations in fiber water content of 3%, 6%, 10%. The test results showed the tensile strength of sugar cane composite with 65% volume fraction has strong value Drag and impact greater than others. Composite of sugarcane fiber with 10% water content has strong value Drag and impact highest than composite with water content of 6% and 3%. Strong value Pull all specimens still not meet BKI standards.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: serat, komposit, tensile strength, impact,
Subjects: V Naval Science > V Naval Science (General)
V Naval Science > VM Naval architecture. Shipbuilding. Marine engineering
Divisions: Faculty of Marine Technology > Marine Engineering > (S1) Undergraduate Theses
Depositing User: retno pujiati
Date Deposited: 10 Oct 2017 02:11
Last Modified: 08 Mar 2019 02:37
URI: http://repository.its.ac.id/id/eprint/46653

Actions (login required)

View Item View Item