Analisa pengaruh variasi temperatur austenisasi terhadap kekerasan, kekuatan impak dan struktur mikro dengan proses laku panas pada baja karbon AISI 1050

Fawaiz, Ismah (2017) Analisa pengaruh variasi temperatur austenisasi terhadap kekerasan, kekuatan impak dan struktur mikro dengan proses laku panas pada baja karbon AISI 1050. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2114030044-Non_Degree.pdf]
Preview
Text
2114030044-Non_Degree.pdf - Published Version

Download (3MB) | Preview

Abstract

Industri-industri pembuatan produk peralatan pertanian seperti pisau igrek dalam produksinya menggunakan perlakuan panas pada material. Oleh karena itu dilakukan penelitian terhadap baja AISI 1050 yang merupakan jenis karbon sedang untuk mengetahui pengaruh variasi temperatur austenisasi terhadap kekerasan, kekuatan impak dan struktur mikro.
Pada penelitian ini dilakukan analisa pada baja AISI 1050. Metodologi penelitian yang digunakan meliputi pemotongan benda uji, uji laku panas dengan variasi temperatur 800oC, 850oC dan 900oC, pengujian kekerasan, pengujian kekuatan impak dan pengujian metallografi.
Dari hasil penelitian pada baja AISI 1050 yang didapat yaitu nilai kekerasan yang tertinggi pada temperatur 800oC sebesar 58 HRC dan nilai kekuatan impak yang tertinggi adalah pada temperatur 900oC sebesar 0,0643 ( J⁄〖mm〗^(2 ) ). Kandungan martensit terbanyak pada temperatur 800oC. Semakin tinggi temperatur maka semakin berkurangnya nilai kekerasan suatu material dan semakin sedikit pula martensit yang terbentuk. Namun pada impak, semakin tinggi temperatur maka nilai kekuatan impak juga semakin naik yang menyebabkan material bersifat ulet.

==================================================================================================

Manufacture industries of agricultural equipment such as igrek knives in their production use heat treatment in the material. Therefore a study of AISI 1050 steel which is a type of medium carbon to determine the effect of austenisation temperature variation on hardness, impact strength and micro structure.
In this research will be analyzed on carbon steel AISI 1050. The methodology used included are material cutting, hardening heat treatment test with temperatur variations 800oC, 850oC and 900oC then hardness test, impact strength test and metallographic test.
From the results of research on carbon steel AISI 1050 obtained the highest hardness value at temperature of 800oC is 58 HRC and the highest impact strength value at temperatur of 900oC is 0,0643 ( J⁄〖mm〗^(2 ) ). The higher martensite is formed at temperatur of 800oC. The higher temperature then getting lower value of material hardness and also causes the less content of martensite which is formed. But at the impact, the higher temperature then the impact strength also getting up which causes the material to be tough.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Hardness Test, Impact Strength Test, Metallography Test
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Ismah Fawaiz
Date Deposited: 13 Oct 2017 06:19
Last Modified: 06 Mar 2019 06:23
URI: http://repository.its.ac.id/id/eprint/46677

Actions (login required)

View Item View Item