Pengaruh Proses Annealing Terhadap Perubahan Kekerasan Dan Struktur Mikro Pada Pipa SA 179 yang Telah Mengalami Pembengkokan

Nugroho, Lanal Septiawan (2017) Pengaruh Proses Annealing Terhadap Perubahan Kekerasan Dan Struktur Mikro Pada Pipa SA 179 yang Telah Mengalami Pembengkokan. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2114030017-Non_Degree.pdf - Published Version

Download (6MB) | Preview

Abstract

Baja paduan adalah baja yang sering digunakan sebagai pipa boiler atau heat exchanger. Kondisi operasional yang ekstrim serta proses pembengkokan pipa menyebabkan perubahan nilai kekerasan, oleh karena itu perlu diberikan heat treatment. Annealing merupakan salah satu metode perlakuan panas yang digunakan untuk memperbaiki sifat mekanik baja. Tujuan penelitian ini adalah untuk melihat pengaruh perlakuan annealing terhadap kekerasan dan struktur mikro baja paduan SA 179. Pada penelitian ini proses annealing dilakukan dengan cara, baja dipanaskan hingga temperatur 850⁰C. Selanjutnya dilakukan pengujian kekerasan untuk mengetahui pengaruh perlakuan panas terhadap perubahan nilai kekerasan, serta dilakukan juga pengamatan melalui mikroskop optic untuk mengetahui struktur mikro material SA 179. Dari hasil pengujian kekerasan, didapatkan bahwa material pipa yang telah dibengkokan mengalami kenaikan kekerasan dari pada pipa sebelum dibengkokan, dan pada saat pipa bengkok dilaku panas dengan proses annealing mengalami penurunan nilai kekerasan. Sedangkan hasil pengujian metalografi pada pipa yang telah dilakukan proses annealing terdapat butir ferrit dan pearlite. Perlakuan annealing menyebabkan ukuran butir menjadi lebih besar dan seragam daripada pipa sebelum dilaku panas. Sehingga terbukti dengan dilakukan proses annealing pada pipa yang telah dibengkokan ini dapat memperbaiki sifat mekanik pipa. ================================================================= Steel alloy is a steel that is often used as a boiler pipe or heat exchanger. Extreme operational conditions and pipe bending processes that are not done properly cause changes in the value of violence, therefore heat treatment is required. Annealing is one method of heat treatment used to improve the mechanical properties of steel. The purpose of this study was to see the effect of annealing treatment on hardness and microstructure of SA 179 alloy steel. In this experiment the annealing process is carried out in a manner the steel is heated to a temperature of 850⁰C, then testing hardness to determine the effect of heat treatment on the change of hardness value and also observation through optical microscope to know the micro structure of SA 179 material. From the results of hardness testing, it was found that the pipe material that has been bending increased the hardness of the pipe before the bending and when the bending pipe heat treatment by annealing process has decreased the hardness value of the bending pipe before the heat treatment. While the results of metallographic testing, on pipes that have been heat treatment by annealing process there are grains of ferrite and pearlite which tend to be more uniform and smoother than the pipe before the heat. So it is proven that by doing annealing process on this bending pipe can improve the mechanical properties of the pipe.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Pengaruh annealing, Proses pembengkokan, Hardness Test, Metalography Test, Effects of Annealing, Bending Process
Subjects: T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
T Technology > TS Manufactures > TS280 Pipe Bending, Tube Bending
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Lanal Septiawan Nugroho
Date Deposited: 13 Dec 2017 05:51
Last Modified: 06 Mar 2019 02:51
URI: http://repository.its.ac.id/id/eprint/47421

Actions (login required)

View Item View Item