Pengaruh Komposisi Dispersant Peg6000 Dan Tio2 Terhadap Kemampuan Self Cleaning Cat Tembok Batu Gamping

Fadhilah, Nur (2016) Pengaruh Komposisi Dispersant Peg6000 Dan Tio2 Terhadap Kemampuan Self Cleaning Cat Tembok Batu Gamping. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2412100097-Undergraduate-Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

Telah dilakukan penambahan TiO2 dan dispersant PEG6000 pada cat tembok batu gamping untuk meningkatkan kemampuan self cleaning cat. Metode yang digunakan adalah pembuatan TiO2 dengan prekursor TiCl3, uji XRD, suspensi TiO2/PEG, uji FTIR, pencampuran pada cat, uji sudut kontak dan self cleaning, uji AFM serta analisa citra menggunakan software imageJ. Berdasarkan hasil pengujian yang telah dilakukan, dengan adanya penambahan TiO2 dan dispersant PEG6000 cukup signifikan untuk meningkatkan kemampuan self cleaning cat tembok batu gamping. Kemampuan self cleaning tertinggi untuk semua kondisi penyinaran proses fotokatalisis diperoleh pada sampel dengan komposisi TiO2 dan PEG sebesar 1 : 6. Dengan nilai yang diperoleh yaitu sudut kontak terkecil 70, persentase luas pengotor yang hilang tertinggi 83,11% dan laju degradasi pengotor terbesar 0,0257cm2/menit. Sampel dengan komposisi TiO2 dan PEG sebesar 1: 6 memiliki distribusi TiO2 lebih merata dengan luas rata-rata partikel adalah 75,81 μm2, dan luas seluruh partikel TiO2 yaitu 2544 μm2 dengan persentase 63,6%. ======================================================================================================================== The addition of TiO2 and dispersant PEG6000 in the paint limestone is to increase the self-cleaning paint proficiency level. The method used is the manufacture of TiO2 with TiCl3 precursors, XRD test, suspension TiO2 / PEG, FTIR test, mixing of paint, the contact angle test and self-cleaning, AFM test and image analysis using ImageJ software. Based on the results of tests that have been conducted, with the addition of TiO2 and dispersant PEG6000, it is enough to improve the ability of self-cleaning paint the walls of limestone. The highest self-cleaning capability for all illumination conditions of the photocatalyst obtained on the sample with a composition of TiO2 and a PEG of 1: 6. With the value obtained by the smallest contact angle of 70, the percentage of residual impurities 16.566% smallest and largest contaminant degradation rate 0.0257 cm2 / min. Sample with a composition of TiO2 and a PEG of 1: 6 have more spread of distribution TiO2 with particle avarage wide 75.81 μm2 , all wide TiO2 is 2544 μm2 by percentage 63.6%.

Item Type: Thesis (Undergraduate)
Additional Information: RSF 553.516 Fad p
Uncontrolled Keywords: TiO2, PEG, batu gamping, self cleaning
Subjects: Q Science > QC Physics
T Technology > T Technology (General)
Divisions: Faculty of Industrial Technology > Physics Engineering > (S1) Undergraduate Theses
Depositing User: Mrs Ansi Aflacha
Date Deposited: 09 Aug 2017 03:31
Last Modified: 09 Aug 2017 03:31
URI: http://repository.its.ac.id/id/eprint/48288

Actions (login required)

View Item View Item