Pengaruh Long Immersing Time Dan Pendinginan Copperized AISI 1006 Terhadap Struktur Mikro Dan Sifat Kekerasan

Zulkifli, . (2016) Pengaruh Long Immersing Time Dan Pendinginan Copperized AISI 1006 Terhadap Struktur Mikro Dan Sifat Kekerasan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2712100028-Undergraduate-Thesis.pdf]
Preview
Text
2712100028-Undergraduate-Thesis.pdf

Download (3MB) | Preview

Abstract

Copperizing merupakan penambahan tembaga
menggunakan teknik hot-dip. Penambahan tembaga dilakukan
karena dapat meningkatkan kekerasan pada baja karbon rendah,
dengan cara memperkecil ukuran butir. Penelitian ini bertujuan
untuk mengetahui pengaruh waktu celup dan pendinginan pada
struktur mikro dan sifat kekerasan copperized AISI 1006 serta
mekanisme penguatannya. Variasi waktu celup yang digunakan
yaitu 10 menit, 20 menit, dan 30 menit serta pendinginan normal
dan cepat (quench). Pengujian yang dilakukan pada penelitian
berupa pengujian spektrometri untuk menganalisis unsur,
pengujian x-ray diffraction untuk mengamati transformasi fasa
yang terbentuk, pengujian metalografi untuk mengamati
perubahan struktur mikro, pengujian SEM EDX untuk mengamati
topologi dan persebaran dari atom tembaga, dan pengujian
microhardness untuk menganalisis kekerasan fasa yang diperoleh
dari sampel uji. Hasil penelitian terlihat bahwa telah terjadi
perubahan struktur mikro dan sifat kekerasan. Struktur mikro yang
diperoleh pada pendinginan normal dan waktu celup 10 menit; 20
menit; dan 30 menit adalah ferrit, ferrit, dan pro-eutectoid ferrit.
Sedangkan struktur mikro yang diperoleh pada pendinginan
quench dan waktu celup 10 menit; 20 menit; dan 30 menit adalah
ferrit, martensit dan bainit. Nilai kekerasan maksimum diperoleh
dengan pendinginan quench dan waktu celup 20 menit sebesar
309,97 HV dikarenakan terbentuknya struktur mikro martensit.
Mekanisme penguatan yang terjadi pada AISI 1006 dengan metode
copperizing adalah pengecilan butir ferrit untuk waktu celup 10
menit pendinginan normal dan quench, serta 20 menit pendinginan
normal. Sedangkan sampel uji lainnya mengalami perubahan
struktur mikro.
========================================================================================================================
Copperizing is the addition of copper using hot-dip
technique. The addition of copper is done to increase the hardness
of low carbon steel, by minimizing the grain size. This study aims
to determine the effect of immersion time and cooling
temperatures on the microstructure and hardness properties of
copperized AISI 1006 and strengthening mechanisms. The time
variation of immerse used is 10 minutes, 20 minutes and 30
minutes as well as normal and rapid cooling (quench). Tests
conducted on the research are spectrometry test to analyze the
elements, x-ray diffraction test to observe the formed of phase
transformation, metallographic test to observe changes in the
microstructure, SEM EDX test to observe the topology and
distribution of the copper atoms, and testing of microhardness to
analyze violence phase obtained from the test sample. Research
results visible changes in the microstructure and hardness
properties. Microstructure obtained in the normal cooling with
immersion time 10 minutes; 20 minutes; and 30 minutes is ferrite,
ferrite and pro-eutectoid ferrite. While the microstructure obtained
in quench cooling with immersion time 10 minutes; 20 minutes;
and 30 minutes is ferrite, martensite and bainite. The maximum
hardness value is obtained by rapid cooling and 20 minutes
immersion time is 309.97 HV due to the formation of martensite
microstructure. The strengthening mechanism that occurs in AISI

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.182 Zul p
Uncontrolled Keywords: AISI 1006, Copperizing, kekerasan, struktur mikro, tembaga.
Subjects: T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Users 13 not found.
Date Deposited: 06 Sep 2017 03:29
Last Modified: 27 Dec 2018 04:31
URI: http://repository.its.ac.id/id/eprint/48797