Pengaruh Kecepatan Putar Dan PH Terhadap Karakteristik Korosi Baja Karbon Rendah Pada Asam Asetat Menggunakan Rotating Cylinder Electrode (RCE)

Hidayatullah, Gilang Maulana (2016) Pengaruh Kecepatan Putar Dan PH Terhadap Karakteristik Korosi Baja Karbon Rendah Pada Asam Asetat Menggunakan Rotating Cylinder Electrode (RCE). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 2712100053-Undergraduate-Thesis.pdf]
Preview
Text
2712100053-Undergraduate-Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

Korosi merupakan bentuk degradasi material yang menyebabkan turunnya sifat mekanik material tersebut. Fenomena korosi ini merupakan sesuatu yang pasti terjadi pada setiap logam. Laju korosi dari suatu material dipengaruhi oleh beberapa faktor diantaranya yaitu nilai pH lingkungan dan karakteristik aliran fluida yang kontak langsung dengan logam. Ada beberapa cara untuk mensimulasikan karakteristik aliran fluida, metode yang digunakan pada penelitian ini yaitu Rotating Cylinder Electrode (RCE), metode tersebut merupakan salah satu metode yang sering digunakan. Pada penelitian ini digunakan baja karbon rendah dan elektrolit Asam asetat dengan pH yaitu 4; 4,5; 5; dan 6 dan variasi kecepatan putaran yaitu 0 rpm, 50 rpm, dan 272 rpm, dengan diameter spesimen 10 mm dan tebal spesimen 10 mm. Pada pengujian weight loss selama 10 hari, didapatkan hasil laju korosi tertinggi pada pH 4 dengan kecepatan putar 272 rpm sebesar 0,4835 mm/y, dan dari pengujian tafel didapatkan 0,2220 mm/y. Hasil pengamatan SEM menunjukkan adanya perbedaan morfologi pada permukaan spesimen karena pengaruh kecepatan putaran. Kecepatan putaran mengakibatkan tergerusnya produk korosi oleh aliran dan menghasilkan profil aliran. Pada pengujian XRD dengan menggunakan spesimen pH 4 dan kecepatan putar 272 rpm hanya ditemukan unsur Fe akibat sedikitnya produk korosi yang ada di permukaan spesimen, sedangkan pada pengujian XRD yang dilakukan pada spesimen dengan pH 4 dan kecepatan putar 0 rpm ditemukan unsur Fe dan senyawa FeOOH sebagai produk korosi.
========================================================================================================================
Corrosion is degradation of the material which cause a decline in the mechanical properties of the material. This corrosion phenomenon happen in every metal. The corrosion rate of a material is influenced by several factors, such as pH value of the environment and the characteristics of the fluid flow in direct contact with the metal. There are several ways to simulate fluid flow characteristics, the method used in this research is the Rotating Cylinder Electrode (RCE), that method is one method that is often used. In this research was used low carbon steel and acetic acid electrolyte with pH 4; 4.5; 5; and 6 and variations in rotation speed of 0 rpm, 50 rpm, and 272 rpm. Specimen diameter is 10 mm and 10 mm thickness. Weight loss test for 10 days, showed the highest corrosion rate at pH 4 with 272 rpm rotating speed of 0.4835 mm/y, and tafel test showed corrosion rate of 0.2220 mm/y. SEM observations showed morphological differences on the surface of the specimen due to the influence of the rotating speed. The rotating speed eroded the corrosion products and produce a flow profile. XRD with specimen pH 4 and rotational speed 272 rpm found only a single element Fe due to little amount of the corrosion products on the surface, while XRD testing with pH 4 and rotational speed 0 rpm found single element Fe and FeOOH compound as corrosion product.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.112 23 Hid p
Uncontrolled Keywords: Asam Asetat, Karakteristik korosi , Rotating Cylinder Electrode, pH.
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Users 13 not found.
Date Deposited: 12 Sep 2017 05:23
Last Modified: 12 Sep 2017 05:23
URI: http://repository.its.ac.id/id/eprint/48830