Esterifikasi Asam Asetat Menggunakan Katalis Zeolit X Dari Kaolin Bangka Belitung

Iftitahiyah, Vita Nur (2017) Esterifikasi Asam Asetat Menggunakan Katalis Zeolit X Dari Kaolin Bangka Belitung. Masters thesis, Institut Teknologi Sepuluh November.

[thumbnail of 1415201004-Master_Thesis.pdf]
Preview
Text
1415201004-Master_Thesis.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Katalis Zeolit X dengan rasio molar SiO2/Al2O3 adalah 4 telah berhasil disintesis menggunakan kaolin sebagai sumber silika dan alumina dengan komponen tambahan yaitu LUDOX (colloidal silica). Padatan dikarakterisasi menggunakan difraksi sinar-X, spektroskopi inframerah (FT-IR), Scanning Electron Microscopy (SEM), piridin FT-IR dan nitrogen adsorpsi-desorpsi. Sampel zeolit telah diketahui sebagai struktur zeolit NaX dari puncak khas pada difraktogram XRD dengan didukung oleh hasil dari FT-IR. Morfologi partikel zeolit dapat dilihat dari hasil SEM. Keasaman permukaan sampel dianalisis dengan FT-IR menggunakan piridin sebagai probe telah menunjukkan sisi asam Lewis dan Brǿnsted yang cukup tinggi. Pengukuran menggunakan nitrogen adsorpsi-desorpsi dilakukan untuk mengetahui luas permukaan sampel yaitu 80,240 m2/g dan ukuran pori sekitar 3,41 nm. Data SEM menunjukkan morfologi zeolit X adalah oktahedral. Aktivitas katalitik sampel HX dipelajari pada reaksi esterifikasi asam asetat dengan benzil alkohol dengan kondisi optimum yaitu pada rasio molar reaktan asam asetat terhadap benzil alkohol 1 : 4 dan waktu reaksi 8 jam, menunjukkan konversi sebesar 58,78%. Konversi pada variasi loading katalis akan meningkat dengan semakin meningkatnya katalis yang ditambahkan. Aktivitas HX dibandingkan H-kaolin menunjukkan konversi yang lebih tinggi. Produk hasil reaksi asam asetat dengan benzil alkohol dikarakterisasi dengan GC-MS yang menunjukkan selektivitas katalis yang tinggi terhadap benzil asetat
========================================================================================================
The catalyst (zeolite X) with a molar ratio of SiO2/Al2O3 = 4 was successfully synthesized using kaolin as a source of silica and alumina with additional components, such as LUDOX (colloidal silica). The sample was characterized using X-ray diffraction, infrared spectroscopy (FT-IR), Scanning Electron Microscopy (SEM), pyridine FT-IR and nitrogen Adsorption-Desorption. Sample was known as zeolite NaX structure based on the specific peaks in the diffractogram of XRD and supported by the results of FT-IR. Morphology particles could be seen from the micrograph of SEM. The acidity was analyzed by FT-IR using pyridine as probe which showed high Lewis and BrØnsted acid sites. Nitrogen adsorption-desorption determined the surface area of sample HX, that is 80.240 m2/g with the pore size about 3,41 nm. SEM micrograph showing the morphology of particle NaX is octahedral. Zeolite HX catalytic activity was studied in the esterification of acetic acid with benzyl alcohol with optimum condition is 1 : 4 ratio and the reaction time is 8 hours, showed the higest conversion (58.78%). The Conversion of catalyst loading variety was improved as the mount of percentage of loading catalyst. HX activity was compared with H-kaolin showing the higher conversion of product. The product of esterification between acetic acid and benzyl alcohol was characterized by GC-MS, showed the better selectivity of benzyl acetate.

Item Type: Thesis (Masters)
Additional Information: RTKi 660.284 4 Ift e-1 3100018074169
Uncontrolled Keywords: Zeolit X, Karakterisasi, Esterifikasi, Benzil Asetat.
Subjects: Q Science > QD Chemistry
Q Science > QD Chemistry > QD305.A2 O73 Esterification
Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions: Faculty of Mathematics and Science > Chemistry > 47101-(S2) Master Thesis
Depositing User: Nur Iftitahiyah Vita
Date Deposited: 19 Feb 2018 03:38
Last Modified: 20 Apr 2020 19:37
URI: http://repository.its.ac.id/id/eprint/49215

Actions (login required)

View Item View Item