Analisis Penambahan Silikon Terhadap Sifat Mekanik Dan Struktur Mikro Pada Paduan Aluminium Silikon Magnesium (Al-Si-Mg) Untuk Aplikasi Piston

Fadly, Eri Dya (2018) Analisis Penambahan Silikon Terhadap Sifat Mekanik Dan Struktur Mikro Pada Paduan Aluminium Silikon Magnesium (Al-Si-Mg) Untuk Aplikasi Piston. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511440000036-Undergraduate_Theses.pdf]
Preview
Text
02511440000036-Undergraduate_Theses.pdf - Accepted Version

Download (6MB) | Preview

Abstract

Piston merupakan komponen mesin yang membentuk ruang bakar dengan silinder blok dan silinder head. Kondisi kerja dari piston berada pada temperatur 350-500OC dan tekanan berkisar 3,5-10 MPa. Oleh karena itu untuk komponen piston motor membutuhkan material yang kuat, serta tidak mengalami kegagalan pada temperatur tinggi. Adapun bahan piston umumnya menggunakan paduan AlSi yaitu logam paduan M124 (AlSi12CuMgNi). Namun untuk mendapatkan sifat mekanik yang maksimal khususnya pada kekerasn dan kekuatan tarik, maka dalam penelitian ini dilakukan pengamatan terhadap penambahan silikon (8, 10, 12, 14%) pada paduan Al-Si-Mg dengan tujuan agar sifat mekaninya meningkat. Metode yang digunakan dalam penelitian ini menggunakan sand casting. Pengujian yang dilakukan untuk menganalisis material ini adalah uji komposisi, uji XRD, uji kekuatan tarik (tensile stress), uji kekerasan, dan uji metalografi,. Setelah pengujian maka didapatkan bahwa logam paduan Al-Si-Mg membentuk fasa α Al, fasa Si dan fasa MgO pada hasil pengujian XRD . Fasa Si terdiri dari bagian terang sedangkan fasa eutektik tersusun lamellar (α Al dan Si) untuk bagin gelap dikarenakan terkorosi pada pengamatan dibawah struktur mikro. Pada hasil uji kekuatan tarik nilai terbesar terdapat pada paduan Al-12Si-Mg sebesar 94,04 Mpa, dan untuk kekerasan terbesar yaitu pada paduan Al-14Si-Mg dengan nilai sebesar 70,98 HV. Sedangkan untuk nilai kekuatan tarik dan kekerasan paling rendah yaitu pada paduan Al-8Si-Mg 84,1 MPa, dan 64,6 HV.
========================================================================================================
Piston is the engine components that form the combustion chamber with cylinder block and cylinder head. The working conditions of the piston are at 350-500OC and pressure ranges from 3.5 to 10 MPa. Therefore, for motor piston components require a strong material, and do not experience failure at high temperatures. The piston material is generally using Alsi alloy that is metal alloy M124 (AlSi12CuMgNi). However, in order to obtain maximum mechanical properties, especially on hardness and tensile strength, in this study, we observed the addition of silicon (8, 10, 12, 14%) in Al-Si-Mg alloy in order to increase the mechanical properties. The method used in this research using sand casting. Tests conducted to analyze this material are compositional test, XRD test, tensile strength test, hardness test, and metallographic test. After testing it was found that Al-Si-Mg alloys form the α Al, Si and MgO phases in XRD test results. The Si phase is composed of bright parts while the eutectic phase is lamellar (α Al and Si) for darkness due to corrosion of observations under the microstructure After testing, it was found that the highest value of tensile strength test was found in Al 12Si-Mg alloy 94,04 Mpa, and for the biggest hardness that is Al-14Si-Mg alloy with value equal to 70,98 HV. As for the value of tensile strength and the lowest hardness is the Al-8Si-Mg 84.1 MPa, and 64.6 HV.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 621.437 Fad a-1 3100018074254
Uncontrolled Keywords: Piston; sand casting; paduan Al-Si-Mg; struktur mikro; sifat mekanik; Al-Si-Mg alloy; microstructure; mechanical properties
Subjects: T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL214 Automobiles--Motors--Pistons and piston rings.
T Technology > TS Manufactures > TS156 Quality Control. QFD. Taguchi methods (Quality control)
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Eri Dya Fadly
Date Deposited: 19 Feb 2018 04:35
Last Modified: 28 Apr 2020 05:32
URI: http://repository.its.ac.id/id/eprint/49283