Abstract
Pengaruh Mg terhadap interaksi betanin dan TiO2 dipelajari melalui eksperimen dan komputasi. Pengaruh Mg terhadap interaksi betanin dan TiO2 diamati melalui karakterisasi FTIR dan UV-Vis DR. Sementara itu, studi komputasi dilakukan melalui perhitungan dengan metode DFT untuk mengetahui ikatan betanin terhadap TiO2 dan Mg-TiO2 serta profil HOMO-LUMO terkait transfer elektron yang terjadi. Hasil UV-Vis DR menunjukkan bahwa jumlah betanin yang terserap dengan adanya Mg-TiO2 tidak menunjukkan perbedaan yang signifikan, sedangkan berdasarkan studi komputasi didapatkan ikatan betanin terhadap Mg-TiO2 lebih kuat dibandingkan TiO2, dimana panjang ikatan betanin terhadap Mg-TiO2 yaitu sebesar 2,160 Å dan terhadap TiO2 sebesar 2,210 Å. Profil HOMO-LUMO menunjukkan bahwa dengan adanya Mg, pada posisi LUMO terlokalisasi di daerah TiO2 yang menunjukkan transfer elektron mengarah pada TiO2. Hasil tersebut menunjukkan bahwa dengan adanya Mg transfer elektron lebih baik dibandingkan tanpa Mg pada senyawa betanin dan TiO2. ==============================================================================================================
The effect of Mg to the betanin and TiO2 interactions has been studied through experiment and computation. The effect of Mg to the betanin and TiO2 interactions was observed through FTIR and UV-Vis DR. Meanwhile, computational study was obtained using DFT calculation to observe betanin bond to TiO2 and Mg-TiO2, as well as HOMO-LUMO profile to observe the electron transfer. The results of UV-Vis DR showed that the amount of betanin absorbed in the presence of Mg-TiO2 did not show any significant difference, whereas the computational study result showed that betanin bond to Mg-TiO2 was stronger than TiO2, wherein the bond length of betanin to Mg-TiO2 was 2,160 Å and to TiO2 was 2,210 Å. The HOMO-LUMO profile showed that the presence of Mg drive the LUMO position localized to the TiO2. This indicate that electron transfer lead to TiO2. These results show that electron transfer is better in the presence of Mg.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSKi 621.312 44 Okt p-1 3100018074456 |
| Uncontrolled Keywords: | betanin; DSSC; Mg; TiO2; transfer elektron; electron transfer |
| Subjects: | Q Science > QD Chemistry T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2960 Dye-sensitized solar cells. Solar batteries. Solar cells |
| Divisions: | Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis |
| Depositing User: | Nanik Ismi Oktavianti |
| Date Deposited: | 06 Mar 2018 02:48 |
| Last Modified: | 31 Aug 2020 03:55 |
| URI: | http://repository.its.ac.id/id/eprint/49819 |
Actions (login required)
 |
View Item |