Analisa Pengaruh Lebar Goresan (SCRATCH) Terhadap Laju Korosi Dengan Variasi Kadar NaCl

Yodanata, Erick Anggi (2014) Analisa Pengaruh Lebar Goresan (SCRATCH) Terhadap Laju Korosi Dengan Variasi Kadar NaCl. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4212106007-Undergraduate Thesis.pdf] Text
4212106007-Undergraduate Thesis.pdf - Published Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Korosi adalah kehancuran atau kerusakan material karena
reaksi dengan lingkungannya . Korosi bisa mengakibatkan
menurunnya kualitas dari baja tersebut sehingga
mengakibatkan baja tersebut menjadi rusak, maka diperlukan
suatu perlindungan coating agar korosi yang terjadi bisa
diperkecil. Sedangkan di lapangan pada saat peluncuran
kapal secara memanjang (End Launching) sering terjadi
goresan pada pelat yang disebabkan permukaan yang tidak
merata sehingga dapat mengurangi ketebalan plat yang
menyebabkan korosi. Sistem coating yang diuji adalah sistem
tiga lapis dengan menggunakan cat Epoxy yang kemudian
diberikan goresan ( Scratch ) dengan lebar yang bervariasi
dan kemudian dicelupkan pada media korosi yaitu NaCl
dengan kadar yang bervarias pula.. Pengujian dan
perhitungan laju korosinya dengan menggunakan metode
elektrokimia. Dari hasil perhitungan dan percobaan dapat
disimpulkan bahwa semakin besar lebar goresan dan kadar
NaCl yang digunakan maka semakin besar pula laju korosi
yang dihasilkan oleh spesimen uji tersebut, sebaliknya
semakin kecil lebar goresan dan kadar NaCl yang digunakan
maka semakin kecil pula laju korosi dari spesimen uji.
=======================================================================================================
Corrosion is the destruction of or damage to property due
to a reaction with its environment. Corrosion can lead to
decreased quality of the steel and causing the steel to be
damaged, we need a protective coating so that the corrosion can
be minimized. While on the ground at the time of the launch
vessel lengthwise (End Launching) often occurs due to scratches
on the plate surface uneven so as to reduce the thickness of the
plate which cause corrosion. Coating system that we were test are
namely the three-layer system using Epoxy paints are then given
a scratch with a width that varies and then dipped to corrosion
media namely NaCl. Testing and calculation of the rate of
corrosion by using an electrochemical method. From the results
of calculations and experiments can be concluded that the greater
the width scratches and NaCl levels that used to, the corrosion
rate also getting bigger and otherwise the smaller the width
scratches and NaCl levels that used to, the corrosion rate also
getting smaller.

Item Type: Thesis (Undergraduate)
Additional Information: RSSP 620.112 23 Yod a
Uncontrolled Keywords: Corrosion and anti corrosives
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions: Faculty of Marine Technology (MARTECH) > Marine Engineering > 36202-(S1) Undergraduate Thesis
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 05 Feb 2018 04:22
Last Modified: 05 Feb 2018 04:22
URI: http://repository.its.ac.id/id/eprint/51126

Actions (login required)

View Item View Item