Pengaruh Kombinasi Aditif PEG dan H2O Terhadap Morfologi Pori Membran Datar Asimetris La0,7Sr0,3Co0,2Fe0,8O3-δ dan La0,7Sr0,3MnO3-δ

Iqbal, Rendy Muhamad (2018) Pengaruh Kombinasi Aditif PEG dan H2O Terhadap Morfologi Pori Membran Datar Asimetris La0,7Sr0,3Co0,2Fe0,8O3-δ dan La0,7Sr0,3MnO3-δ. Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 01211550012001_Master Thesis.pdf]
Preview
Text
01211550012001_Master Thesis.pdf - Accepted Version

Download (6MB) | Preview

Abstract

Membran perovskit (La0,7Sr0,3Co0,2Fe0,8O3-δ dan La0,7Sr0,3MnO3-δ) merupakan membran asimetris yang mampu menghantarkan oksigen dan dapat dimanfaatkan untuk berbagai keperluan seperti pemisahan gas, solid oxide fuel cell dan oksidasi parsial metana. Kemampuan membran perovskit dalam menghantarkan oksigen dipengaruhi oleh morfologi dan struktur pori membran. Membran dengan morfologi asimetris (memiliki lapisan rapat dan berpori) memiliki kinerja yang baik untuk menghantarkan oksigen. Morfologi membran dapat didesain dengan penambahan aditif pada larutan dope. Penelitian ini dilakukan untuk mengetahui pengaruh aditif terhadap morfologi dan struktur pori, serta kinerja untuk menghantarkan oksigen dari membran perovskit. Aditif yang digunakan pada penelitian ini yaitu Polietilen Glikol (PEG) dengan berat molekul 8000 dan air, serta variasi rasio PEG : H2O = 5 : 0 ; 4,5 : 0,5; 4 : 1 dan 3,5 :1,5 % berat. Karakterisasi kristal perosvkit dengan XRD, sedangkan morfologi dan struktur pori membran diamati dengan Scanning Electron Microscope (SEM). Selain itu, membran yang masih mengandung polimer dikarakterisasi dengan TGA. Pengaruh aditif terhadap kinerja membran juga diamati dengan pengukuran fluks oksigen. Hasil SEM menunjukkan bahwa hampir semua membran asimetris yang difabrikasi memiliki struktur pori finger like dengan lapisan rapat yang tipis. Selain itu, hasil pengukuran fluks oksigen membran datar LSCF 7328 dengan rasio PEG : H2O = 0 : 0, 4 : 1 dan 5 : 0 % berat memiliki nilai masing-masing 2.10-7; 3,98.10-7 dan 6,67.10-7 mol.s-1.cm-2.
================================================================================================================== Perovskite membrane (La0,7Sr0,3Co0,2Fe0,8O3-δand La0,7Sr0,3MnO3-δ) is asymmetric membrane that has ability to transfer oxygen and its can utilizate for gas separation, solid oxide fuel cell, and partial oxidation of methane. The ability to transfer oxygen on perovskite membrane influenced by morphology and pore structure. The membrane that has asymmetric structure was having better performan
ce for oxygen conducting.The aim of this research is to studying influence of aditif on morphology, pore structure, and performance for oxygen conducting
of perovskite membrane. In this research, Combination between PEG 8000 and H2O use as additive and its variated from 5 : 0, 4,5 : 0,5, 4 : 1, and 3,5 :1,5% berat.
. Crystal structure of perovskite is characteriz
ed by XRD. Meanwhile, morphology and pore structure of membrane determined by Scanning Electron Microscopy
(SEM). Membrane which still contain polymer should characterized by TGA. Performance of perovskite membrane was determined by the measurement of oxygen flux. SEM result represent each asymmetric membrane has finger like structure of their pores and dense layer also appear on cross section membrane. Moreover, oxygen flux value of
LSCF 7328 with PEG : H2O ratio =0 : 0, 4 : 1 dan 5 : 0 wt%
were 2.10-7; 3,98.10-7dan 6,67.10-7mol.s-1.cm-2, espectively.

Item Type: Thesis (Masters)
Additional Information: RTKi 549.528 Iqb p
Uncontrolled Keywords: Membran perovskit; La0,7Sr0,3Co0,2Fe0,8O3; La0,7Sr0,3MnO3; Aditif
Subjects: Q Science > Q Science (General)
T Technology > TP Chemical technology > TP248.25.M46 Membrane separation
Divisions: Faculty of Natural Science > Chemistry > 47101-(S2) Master Thesis
Depositing User: Iqbal Rendy Muhamad
Date Deposited: 02 May 2018 03:58
Last Modified: 29 Jun 2020 06:06
URI: http://repository.its.ac.id/id/eprint/51136

Actions (login required)

View Item View Item