Probing Porisitas Lapisan Nano Logam Oksida Dan Penetrasi Bahan Pewarna Sel Surya Dengan Spektroskopi Plasmon Permukaan

Chalimah, Siti (2015) Probing Porisitas Lapisan Nano Logam Oksida Dan Penetrasi Bahan Pewarna Sel Surya Dengan Spektroskopi Plasmon Permukaan. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1112201020-Master Thesis.pdf - Published Version

Download (2MB) | Preview

Abstract

Fenomena Resonansi Plasmon Permukaan (Surface Plasmon Resonance, yang sering disingkat sebagai SPR) sangat sensitif terhadap variasi permitivitas dari lapisan dielektriknya. Tesis ini melaporkan hasil kajian untuk melihat apakah fenomena SPR dapat digunakan untuk membedakan derajat porisitas dari suatu lapisan logam oksida dan penetrasi bahan fungsional organik di dalam struktur porosnya. Penentuan porisitas hingga skala mikrometer dapat dilakukan dengan beberapa cara yang telah baku. Akan tetapi, tidak demikian halnya untuk mengetahui porisitas berukuran nanometer, khususnya dalam bentuk lapisan tipis. Dalam tesis ini, ZnO terdoping Al (AZO) digunakan sebagai logam oksidanya dan ruthenium dye N719 sebagai bahan organik fungsional, yang keduanya merupakan bahan yang sering dipakai dalam sel surya generasi ketiga. Telah diketahui sebelumnya, bahwa nano-morfologi permukaan dari lapisan AZO sangat dipengaruhi oleh konsentrasi dopan Al-nya. Untuk itu telah dilakukan pengukuran spektrum SPR dengan menggunakan sistem pengukuran SPR dengan elemen pengkopel berupa prisma. Hasil pengukuran menunjukkan dip spektrum SPR yang bergantung pada variasi kadar dopan Al-nya. Semakin besar kadar dopan Al, dip spektrum SPR-nya bergeser ke daerah panjang gelombang yang lebih kecil. Hal tersebut dapat mengindikasikan penurunan nilai indeks bias lapisan AZO, sebagai akibat membesarnya derajat porisitas lapisan. Semakin lama waktu perendaman ruthenium dye N719, dip spektrum SPR menunjukkan pergeseran ke daerah panjang gelombang yang lebih besar, yang mengindikasikan bertambahnya penetrasi bahan tersebut pada lapisan mesoporos AZO. ========================================================================================================= The physical phenomenon of (Surface Plasmon Resonance which is often shortened as SPR), is so sensitive toward various permittivity of its dielectric layer. In this thesis, we report our study to characterize whether phenomenon of SPR effect can be used to distinguish the poresity degree of Al-Doped ZnO (AZO) layer and characterize penetration of functional organic material in porous AZO. A porous degree at micro- scale can be characterized by some permanent measurements. Nevertheless, we have difficulty to determine a porous degree of nano-scale material. In this thesis, Al-doped ZnO as metal-oxide and ruthenium dye N719 as a functional organic material. Both of which are often used as thirdgeneration solar cell. It has previously been reported that nano-marphology of AZO is greatly influenced by concentration of Al dopant.We tried to characterize using spectral SPR sensing by prism coupling method. Measurement results are indicated that dip of the spectral SPR depends on various Al dopant concentration. The greater Al dopant concentration is, the smaller dip SPR is. Those are indicated that the greater Al dopant concentration is , the smaller the effectively refractive index of AZO is. The longer the soaking time in ruthenium dye N719 is , the greater dip SPR is. Those are indicated the high penetration toward AZO mesoporous layer.

Item Type: Thesis (Masters)
Additional Information: RTFi 667.2 Cha p
Uncontrolled Keywords: AZO, ZnO, ruthenium dye N719, Surface Plasmon Resonance
Subjects: Q Science > QC Physics
Divisions: Faculty of Mathematics and Science > Physics > (S2) Master Theses
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 19 Mar 2018 06:33
Last Modified: 24 Aug 2018 02:12
URI: http://repository.its.ac.id/id/eprint/51563

Actions (login required)

View Item View Item