Studi Perbandingan Karakteristik Suhu Transisi, Struktur Mikro Dan Sifat Kekerasan Pada Logam Induk, Logam Las Dan Daerah Pengaruh Panas (HAZ) Baja Tahan Karat AISI 304 Setelah Diannealing Pada Bermacam-Macam Suhu

Harris, Abdi SM (2003) Studi Perbandingan Karakteristik Suhu Transisi, Struktur Mikro Dan Sifat Kekerasan Pada Logam Induk, Logam Las Dan Daerah Pengaruh Panas (HAZ) Baja Tahan Karat AISI 304 Setelah Diannealing Pada Bermacam-Macam Suhu. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
4198100035-Undergraduate-Thesis.pdf - Published Version

Download (10MB) | Preview

Abstract

Studi perbandingan karakteristik suhu transisi, struktur mikro dan sifat kekerasan dilakukan pada Iogam induk, logam las dan daerah pengaruh panas baja tahan karat AISI 304 setelah diannealing pada suhu antara 1008°C sampai 1120 °C. Suhu pada pengujian impak dilakukan pada bermacam macam .suhu, suhu terendah -196°C (suhu cryogenic) dan suhu tertinggi 31 °C (suhu kamar), dimana pengujian ini dilakukan untuk memperoleh kurva suhu transisi pada logam induk, Iogam las dan daerah pengaruh panas (HAZ) yang menunjukkan hubungan antara prosentase kepecahan ulet-getas (shear fracture) dengan suhu. Suhu transisi yang paling rendah terletak pada daerah HAZ dan yang paling tinggi terletak pada daerah logam las. Uji kekerasan pada logam induk, logam las, dan daaerah pengaruh panas (HAZ) dilakukan dengan pengujian kekerasan vickers, dimana pengujian ini menggunakan piramida intan sebagai penekan (indentor).Hasil uji kekerasan pada baja AlSl 304 dengan perlakuan menunjukan nilai kekerasan logam las<logam induk<daerah pengaruh panas (HAZ), sedangkan tanpa perlakuan menunjukkan nilai kekerasan Logam dasar<logam las<daerah pengaruh panas (HAZ). Gambar mikrostruktur logam induk, logam las dan daerah pengaruh panas (HAZ) dengan perbesaran 400 X diambil dengan menggunakan foto mikro setelah terlebih dahulu digosok dan dietsa. Hasil foto mikro menunjukkan adanya presipitasi karbida krom (Cr23C6) pada daerah pengaruh panas (HAZ) yang dapat mengurangi ketangguhan dan ketahanan korosi, terbentuknya butir-butir baru yang equiaxe pada daerah logam dasar sehingga terjadi penurunan nilai kekerasan dan kekuatan Jogam, struktur dendritik pada logam las yang terdiri austenitik dan delta ferrite . ============================================================ The comparison characteristic of base metal, weld metal and heat affective zone (1-lAZ) of stainless steels AISI 304 was studied in impact test, hardness test and microstructure after heat treated by annealing which temperature betwen 1008°C to 1120 oc. The temperature of impact test was held in various, the low temperature was -196°C (the cryogenic temperature) and the higher temperature was 31 oc (room temperature) and it was to aimed the transition temperature curves of percentage shear fracture versus temperature each of the three elements (base metal, weld metal and heat affective zone) of speciments.The lowest transition temperature was on heat effective zone and the higher transition temperature was on weld metal. Hardness test was using vickers test with diamond pyramid indentor to resulted the hardness value of base metal, weld metal and heat affective zone (HAZ).The resulted of hardness test on stainless steel AISI 304 with heat treatment shown hardness value of weld metal<base metal<heat effective zone (HAZ), and without heat treatment shown hardness value of base metal<weld metal<heat effective zone (HAZ). Microstructure image of base metal, weld metal and heat affective zone (HAZ) magnified 400 X was taken by using photo micro after the three elements had polished and etsa treated. Foto micro result of heat effective zone (HAZ) showing chromium carbide was precipitated in which reducing corrosion resistance and toughness, new equiaxe grains in which reducing hardness value and strength of steel was created., dendritic structure of weld metal contains austenitic and delta ferrite.

Item Type: Thesis (Undergraduate)
Additional Information: RSPe 671.36 Har s
Subjects: Q Science > QC Physics > QC271 Temperature measurements
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Marine Technology > Naval Architecture and Shipbuilding Engineering > (S1) Undergraduate Theses
Depositing User: ansi aflacha
Date Deposited: 02 Apr 2018 08:34
Last Modified: 02 Apr 2018 08:34
URI: http://repository.its.ac.id/id/eprint/51671