Pengaruh Penggunaan Agregat Ringan Buatan (ALWA) Berbahan Styrofoam dengan Bahan Tambah Serat Baja Pada Beton Ringan Terhadap Kuat Tekan Beton

Wulandari, Meity (2018) Pengaruh Penggunaan Agregat Ringan Buatan (ALWA) Berbahan Styrofoam dengan Bahan Tambah Serat Baja Pada Beton Ringan Terhadap Kuat Tekan Beton. Masters thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
03111650020014-Master_Thesis.pdf - Published Version
Restricted to Repository staff only

Download (9MB) | Request a copy

Abstract

Saat ini sudah banyak inovasi untuk mengganti agregat khususnya agregat kasar dengan agregat ringan buatan yang disebut dengan ALWA (Artificial Light Weight Aggregate). Bahan yang digunakan untuk pembuatan agregat ringan buatan (ALWA) adalah Styrofoam. Penggunaan Styrofoam sebagai bahan campuran untuk pembuatan beton akan mengurangi berat volume beton karena karakteristiknya yang ringan. Styrofoam akan dilarutkan dengan aseton dan dibentuk menjadi butiran dengan ukuran yang menyerupai agregat kasar kemudian dikeringkan agar teksturnya menjadi keras. Pada penelitian ini Serat baja (fiber steel) juga digunakan sebagai bahan tambah, karena dengan penambahan serat baja beton akan lebih tahan terhadap retak sehingga diharapkan mampu meningkatkan kuat tekan. Penelitian ini bertujuan untuk mengetahui pengaruh penggunaan ALWA berbahan Styrofoam dengan bahan tambah serat baja pada beton ringan terhadap kuat tekan, kuat tarik belah dan kuat lentur, serta untuk mengetahui komposisi optimum penggunaan ALWA berbahan Styrofoam dan serat baja sebagai pengganti agregat kasar. Benda uji yang digunakan dalam penelitian ini adalah silinder dengan ukuran 100x200 mm untuk uji kuat tekan dan kuat tarik belah, serta balok ukuran 15x15x600 mm puntuk uji kuat lentur. Mutu beton (f’c) rencana adalah 30 MPa. Komposisi campuran Styrofoam masing-masing 0%, 15%, 50%, dan 100%. Sedangkan komposisi serat baja (fiber steel) masing-masing 0%, 0,75% dan 1,5% dengan diameter kawat 0,7 mm. Hasil penelitian menunjukkan beton dengan campuran 15% ALWA Styrofoam dan 1.5% Serat baja mampu menghasilkan kuat tekan optimum sebesar 28.5 MPa dan modulus elastisnya sebesar 23495 MPa. Hasil pengujian kuat tarik belah yang paling optimum sebesar 5.29 MPa dan untuk hasil uji kuat lentur sebesar 6.43 MPa. ============= Currently there are many innovations to replace aggregate especially coarse aggregates with artificial lightweight aggregates called ALWA. The material used to make ALWA is Styrofoam. The use of Styrofoam as a mixed material for the manufacture of concrete will reduce the weight of the volume of concrete due to its mild characteristics. Then formed into granules then dried to texture becomes hard. In this study Steel fibres is also used as an added material, because with the addition of concrete steel fibers will be more resistant to cracks so it is expected to increase the compressive strength. The purpose of this research is to know the effect of ALWA using Styrofoam material with steel fiber added material on lightweight concrete to compressive strength, tensile strength and flexural strength, and to know the optimum composition of ALWA made from Styrofoam and steel fiber in lieu of aggregate. The test specimens used in this study were cylinders with size 100x200 mm for compressive strength test and tensile strength, and beam size 15x15x600 mm for bending strength test. The quality of the concrete (f'c) plan is 25 MPa. Styrofoam mixture compositions are 0%, 15%, 50%, and 100%, respectively. While the composition of steel fiber (fiber steel) each 0%, 0.75% and 1.5% with a diameter of 0.7 mm wire. The results showed that 15% concrete with ALWA Styrofoam and 1.5% steel fiber was able to produce optimum compressive strength of 28.5 MPa and modulus of elasticity of 23495 MPa. The most optimum tensile strength test result is 5.29 MPa and for the flexural strength test results of 6.43 MPa.

Item Type: Thesis (Masters)
Uncontrolled Keywords: Agregat ringan buatan; ALWA; beton ringan; Styrofoam; aseton; serat baja; kuat tekan; modulus elatisitas; kuat tarik belah; kuat lentur.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA440 Concrete--Cracking
T Technology > TA Engineering (General). Civil engineering (General) > TA441 Aggregates
Divisions: Faculty of Civil Engineering and Planning > Civil Engineering > (S2) Master Theses
Depositing User: Meity Wulandari
Date Deposited: 04 Jul 2018 06:41
Last Modified: 04 Jul 2018 06:41
URI: http://repository.its.ac.id/id/eprint/51938

Actions (login required)

View Item View Item