Analisis Pengaruh Variasi Temperatur dan Media Pendingin Pada Proses Hardening Material AISI 8655 Terhadap Sifat Mekanik Kekerasan dan Struktur Mikro Untuk Hammer Crusher PT. Semen Indonesia

Permadi, Reza Fauzan (2018) Analisis Pengaruh Variasi Temperatur dan Media Pendingin Pada Proses Hardening Material AISI 8655 Terhadap Sifat Mekanik Kekerasan dan Struktur Mikro Untuk Hammer Crusher PT. Semen Indonesia. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511440000126-Undergraduate_Theses.pdf - Published Version
Restricted to Repository staff only

Download (7MB) | Request a copy

Abstract

Clinker cooler adalah alat yang digunakan setelah material keluar dari mesin kiln yang berfungsi sebagai pembentuk terak (clinker). Clinker cooler mentransportasikan terak ke hammer crusher. Hammer crusher merupakan salah satu bagian dari clinker cooler yang berfungsi untuk menghancurkan terak (clinker) yang dihasilkan oleh kiln. Hammer crusher bekerja bersamaan dengan rotor yang berputar dan menghantam terak (clinker) yang ada. Hammer crusher digunakan secara terus menerus dan terjadi keausan pada material hammer crusher. Hal ini menyebabkan umur hammer crusher menjadi berkurang. Dalam penelitian ini, dilakukan analisis kegagalan dari hammer crusher dan solusi dari kegagalan tersebut berupa hardening. Setelah dilakukan pengujian komposisi, material yang digunakan adalah AISI 8655 dan tidak sesuai dengan standar, yaitu ASTM A532. Solusi yang dilakukan menggunakan perlakuan panas pada material hammer crusher agar kekerasannya meningkat adalah dengan dipanaskan hingga temperatur 820oC dan 870oC dengan waktu tahan 2,5 jam, yang kemudian di quench dengan media pendingin oli, air, dan udara. Setelah itu spesimen ditempering di temperatur 213oC selama 1 jam. Kemudian dilakukan uji metalografi, uji kekerasan, uji impak dan uji abrasif. Setelah pengujian dilakukan, didapatkan hasil berupa kekerasan dan ketahanan aus maksimal pada temperatur 870oC dengan media pendingin brine dengan kekerasan 532 HV dan laju keausan sebesar 0.0933 gram. Kekerasan dan ketahanan aus paling rendah didapatkan pada temperatur 820oC dengan media pendingin oli sebesar 461 HV dan 0.2067 gram. ============ Clinker cooler is a tool that use after material going out from klin machine which made clinker. Clinker cooler transport clinker to hammer crusher. Hammer crusher is a part of clinker cooler that use to make clinker smaller. Hammer crusher work together with rotating rotor and hit the clinker. Hammer crusher work continously and became wear. This thing made hammer crusher’s life time reduced. In this study, performed a failure analysis of the hammer crusher and the solution of failure with hardening. After composition test, the failure is found because using material AISI 8655 which not as a standard, ASTM A532. The solution did with heat treatment of hammer crusher for increasing the hardness is with hardening until temperature 820oC and 870oC and holding time 2,5 hours then quench with cooling media oil, water, and brine. After that the specimen tempered in temperature 213oC for 1 hour. Then doing metallography test, hardness test, impact test, and wear test. After doing the test, the maximal hardness and wear rate is at 870oC with brine cooling media for 532 HV and 0.0933 gram. The minimum hardness and wear rate is at 820oC with oil cooling media for 461 HV and 0.2067 gram.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Hammer Crusher, AISI 8655, Clinker Cooler, Kekerasan, Keausan, Hammer Crusher, AISI 8655, Clinker Cooler, Hardness, Wear.
Subjects: Q Science > QC Physics > QC 611.97.T46 Temperature effects. Including transition temperature
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Reza Fauzan Permadi
Date Deposited: 22 Nov 2018 04:16
Last Modified: 22 Nov 2018 04:16
URI: http://repository.its.ac.id/id/eprint/52922

Actions (login required)

View Item View Item