Pengaruh konsentrasi Ag pada lapisan tipis komposit kitosan/Agnps terhadap sifat antimikroba, biokompatibilitas, dan adhesi sebagai aplikasi implan ortopedi

Mobiliu, Raditya Noorachman (2018) Pengaruh konsentrasi Ag pada lapisan tipis komposit kitosan/Agnps terhadap sifat antimikroba, biokompatibilitas, dan adhesi sebagai aplikasi implan ortopedi. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511440000084-Undergraduate_Theses.pdf - Published Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Biomaterial telah lama digunakan sebagai material implan ortopedik. Pengimplanan material tersebut beresiko menimbulkan adhesi bakteri yang dapat menyebabkan terbentuknya biofilm yang dapat menimbulkan infeksi pada tubuh manusia. Upaya untuk mengatasi infeksi pada implan yang disebabkan bakteri telah banyak dilakukan oleh banyak peneliti. Nanopartikel Ag berpotensi sebagai material antimikroba dan kitosan memiliki sifat toksisitas yang rendah. Penelitian ini dilakukan untuk menganalisis pengaruh konsentrasi Ag terhadap morfologi, sifat antimikroba, dan biokompatibilitas dari lapisan tipis kitosan/AgNPs yang dideposisikan menggunakan metode elektroforesis dengan substrat SS 316L serta variasi konsentrasi Ag 0; 0,5; 1; 1,5 mM. Pengujian SEM dan XRD dilakukan untuk mengobservasi morfologi , Kirby/Bauer Test dan MTT assay dilakukan untuk mengobservasi sifat antimikroba dan biokompatibilitas, serta pengujian Pull-off Test digunakan untuk mengobservasi adhesi dari lapisan tipis kitosan dan kitosan/AgNPs. Penambahan konsentrasi Ag meningkatkan kandungan Ag dan terbentuknya partikel nano Ag yang teraglomerasi dan tidak memberikan perubahan signifikan pada ketebalan. Penambahan konsentrasi Ag meningkatkan sifat antimikroba yang ditandai dengan luas zona hambat bakteri untuk sampel SS, 0 mM, 0,5 mM, 1 mM, dan 1,5 mM secara berurutan sebesar 0; 9,57±3,574; 37,35±5,530; 49,20±6,873; dan 57, 48±3,592 mm2.serta menurunkan sifat biokompatibilitas yang ditandai dengan menurunnya cell viability yakni 43%, 27%, 23%, 17%, 12% untuk 24 jam waktu inkubasi dan 42%, 27%, 19%, 10%, 9% untuk 48 jam waktu inkubasi Penambahan konsentrasi Ag tidak memberi perubahan signifikan pada sifat adhesi lapisan. Sifat adhesi lapisan yang dinyatakan oleh kekuatan tarik untuk sampel dengan konsentrasi Ag 0; 0,5; 1; dan 1,5 mM berturut-turut adalah 1,705±0,969; 1,445; 2,255±0,544; dan 2,615±1,916 MPa. ================ Biomaterial had been used for a long time as orthopaedic implant material. The inserting process posses infection risk in bacterial adhesion form that continues into biofilm forming which could infect human body. Preventive actiosn toward implant bacterial infection was done by many researchers. Ag nanoparticles have potential as antimicrobial materials while chitosan has low toxicity. Recent study was done to analyze Ag concentration's effect on morphology, antimicrobial properties, and biocompatibility of chitosan/AgNPs composite thin film which deposited on SS 316L by electrophoretic process. The Ag concentrations were varied, they were chitosan (0 mM); 0,5; 1; and 1,5 mM. SEM characterization was used to observe the morphology and thickness, XRD was used to identify the elements and compounds, FTIR was utilized to study the functional groups, Kirby/Bauer Test and MTT Assay were used to observe the antimicrobial and biocompatibility properties, and Pull-off Test was used to observe the adhesivity of coating on substrate. Increasing Ag concentration increased Ag content and caused the agglomeration of Ag nanoparticles and didn't give any significance change to the film thickness. Escalating Ag concentration enhanced antimicrobial properties which is shown by increasing bacterial inhibition zone area from SS, 0 mM to 1,5 mM sample respectively 0; 9,57±3,574; 37,35±5,530; 49,20±6,873; and 57, 48±3,592 mm2. While on the other side, the biocompatibility declined shown by lowering of the cell viability percentage from 43%, 27%, 23%, 17%, 12% for 24 hours of incubation time, and 42%, 27%, 19%, 10%, 9% for incubation time with 48 hours. Enchancing Ag concentration doesn't give any significance to film adhesion expressed by tensile strength for 0; 0,5; 1; and 1,5 mM samples respectively 1,705±0,969; 1,73; 2,255±0,544; and 2,615±1,916 MPa.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.732 Mob p-1
Uncontrolled Keywords: Kitosan, AgNPs, Elektroforesis, Antimikroba, Biokompatibilitas, Chitosan, AgNPs, Electrophoresis, Antimicrobial , Bio compatibility
Subjects: Q Science
Q Science > QR Microbiology > QR96.8 Adhesion
R Medicine > R Medicine (General)
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Mobiliu Raditya Noorachman
Date Deposited: 19 Dec 2018 07:09
Last Modified: 19 Dec 2018 07:09
URI: http://repository.its.ac.id/id/eprint/52942

Actions (login required)

View Item View Item