Studi Pengaruh Variasi Agregat Limbah Plastik LDPE/PET/Styrofoam Terhadap Sifat Fisik dan Mekanis Komposit Berbasis Semen Portland Untuk Aplikasi Breakwater

Bibra, Muhammad Irfan (2018) Studi Pengaruh Variasi Agregat Limbah Plastik LDPE/PET/Styrofoam Terhadap Sifat Fisik dan Mekanis Komposit Berbasis Semen Portland Untuk Aplikasi Breakwater. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511440000014 - Undergraduate_Thesis.pdf]
Preview
Text
02511440000014 - Undergraduate_Thesis.pdf - Accepted Version

Download (5MB) | Preview

Abstract

Indonesia adalah negara kepulauan dengan kurang lebih 17.000 pulau dan 80.000 km garis pantai (daerah yang dikelilingi oleh pantai-pantai) dengan berbagai potensinya untuk dimanfaatkan dan dikembangkan. Namun, kondisi pantai-pantai di Indonesia cukup dinamis terhadap abrasi yang disebabkan oleh angin dan aktivitas gelombang laut. Dibutuhkan struktur pemecah dan penahan gelombang air laut yang biasa disebut breakwater untuk mereduksi gelombang air laut sehingga kegiatan disekitar pantai dapat dilakukan. Disisi lain sampah plastik sudah menjadi persoalan yang sangat serius terutama di Indonesia. Indonesia menjadi negara penyumbang sampah plastik terbanyak kedua setelah Tiongkok. LDPE dan PET adalah salah satu jenis plastik yang banyak digunakan oleh manusia sehingga menjadi salah satu penyumbang terbesar sampah plastik di dunia khusunya di Indonesia. Sehingga dibutuhkan rekayasa limbah plastik LDPE dan PET untuk mengurangi sampah limbah plastik. Oleh karena itu dalam penelitian ini, dilakukan penelitian penggunaan limbah plastik LDPE, PET, dan Styrofoam sebagai agregat untuk alternatif pembuatan struktur penahan dan pemecah gelombang sekaligus rekayasa limbah plastik. Tujuan penelitian adalah menganalisis pengaruh variasi agregat limbah plastik LDPE/PET/Styrofoam terhadap sifat fisik dan sifat mekanik komposit berbasis semen Portland untuk aplikasi breakwater dan menganalisis komposisi komposit optimal untuk aplikasi breakwater. Proses pembuatan komposit dilakukan dengan pelelehan limbah plastik LDPE, PET, dan Styrofoam lalu dipotong untuk mendapatkan ukuran yang kecil. Selanjutnya dilakukan pengadukan semen, pasir, dan agregat limbah plastik lalu dituang kedalam cetakan komposit. Kemudian dilakukan uji densitas, uji water absorbability, uji FTIR, uji SEM, uji mass loss dan uji kuat tekan. Setelah pengujian dilakukan, didapatkan hasil berupa nilai densitas tertinggi sebesar 2.06 g/cm3 dengan persentase water absorbability terendah sebesar 6.02%. Nilai kuat tekan maksimal adalah 18.8 MPa dan persentase mass loss terendah adalah sebesar 0.03%. ========== Indonesia is an archipelagic country with approximately 17,000
islands and 80,000 km of coastline (the area surrounded by
beaches) with various potentials to be utilized and developed.
However, coastal conditions in Indonesia are quite dynamic
against abrasion caused by wind and sea wave activity. So, it
needed a structure to break and withstand the sea wave, that
called breakwater. Breakwater reduced the sea wave so activities
ain the coastal area can be done. On the other hand plastic waste
has become a very serious problem, especially in Indonesia.
Indonesia became the second largest contributor of plastic waste
after China. LDPE and PET are one of the plastic that used by
human, which caused LDPE and PET to contribute a lot to plastic
waste in the world, especially in Indonesia. So that needed plastic
waste engineering to reduce plastic waste of LDPE and PET. In
this research, the study of the influence of agregate of waste
plastic of LDPE, PET, and Styrofoam as an alternative to the
manufacture of retaining and breaking structures as well as
engineering of plastic waste. The purpose of this research are to
study the influence of plastic waste aggregate
LDPE/PET/Styrofoam to physical and mechanical properties of
Portland cement based composite. The composite making process
is done by melting the waste of plastic LDPE, PET, and
Styrofoam and then cut to get a small size. Further stirring of
cement, sand, and aggregate of plastic waste is then poured into
x
the composite mold. Then do density test, water absorbability
test, FTIR test, SEM test, weight loss test and compressive
strength test. After testing done, the result are the the highest
density value is 2.06 g/cm3 with the lowest water absorbability
percentage is 6.02%. The highest compressive strength value is
18.8 MPa and the lowest mass loss percentage is 0.03%.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Breakwater, Komposit, LDPE, PET, Styrofoam, komposit, Composite
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA441 Aggregates
T Technology > TP Chemical technology > TP884.L5 Lightweight concrete
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Muhammad Irfan Bibra
Date Deposited: 24 Nov 2018 03:10
Last Modified: 22 Apr 2021 03:24
URI: http://repository.its.ac.id/id/eprint/53027

Actions (login required)

View Item View Item