Iskandar, Muhammad Nur (2018) Pengaruh Ketebalan Polycaprolactone Coating Terhadap Morfologi dan Laju Degradasi Paduan Mg-5%Zn Untuk Aplikasi Biodegradable Orthopedic Devices. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511440000138_Muhammad_Nur_Iskandar_TA_Full.pdf - Accepted Version Download (4MB) | Preview |
Abstract
Kasus patah tulang masih sangat tinggi, dan kebutuhan akan implan juga meningkat dengan penggunaan material yang digunakan berupa stainless steel yang sangat beresiko karena dalam aplikasinya dibutuhkan operasi pengangkatan yang membuat kekuatan tulang tidak seperti awal mula sebelum patah. Oleh karena itu banyak dikembangkan bahan implan biodegradable yang akan terdegradasi sendiri tanpa adanya operasi kedua. Paduan Magnesium telah banyak menarik perhatian sebagai bahan implan biodegradable yang potensial, namun masih mempunyai tingkat laju degradasi yang cukup tinggi. Oleh karena itu pada penelitian ini dilakukan penambahan lapisan polycaprolactone (PCL) dengan variasi ketebalan 1 layer, 3 layer, 5 layer dan 7 layer kepada paduan Mg-5%Zn untuk dilihat pengaruhnya terhadap morfologi dan laju degradasinya. Metode yang dilakukan menggunakan metode spray coating. Karakterisasi X-Ray Diffraction (XRD) dilakukan untuk melihat senyawa yang terbentuk dalam paduan Mg-5%Zn, dan senyawa yang didapatkan adalah α-magnesium dan intermetalik MgZn. Pada karakterisasi Scanning Electron Microscope (SEM) menunjukkan dengan bertambahnya ketebalan lapisan PCL hingga ±70μm, secara morfologi berefek pada porositas yang muncul menjadi cendrung lebih kecil dan jarang. Lalu pada pengujian In-vitro berupa Simulated Body Fluid (SBF) untuk menghitung laju degradasi yang terjadi, didapatkan laju degradasinya menurun hingga 1,55 cm/tahun, dan dari uji kelekatan tape test didapatkan kekuatan adhesinya semakin meningkat hingga grade 4B menurut ASTM D3995==============================================================================================================The bone fracture case is still very high, and the need for implants also increases with the use of stainless steel material which is very risky because its application requires surgical removal that makes bone strength unlike the beginning. Therefore many developed research about biodegradable implant materials that will be degraded themselves without any second operation. Magnesium Alloy has attracted much attention as a potential biodegradable implant material, but still has a high rate of degradation. Therefore in this research, the addition of polycaprolactone layer (PCL) with variation of thickness of 1 layer, 3 layer, 5 layer and 7 layer to Mg-5% Zn alloy and its effect on morphology and degradation rate. The research in this methods were performed using spray coating method.. Characterization X-Ray Diffraction (XRD) was performed to see the component formed in Mg-5%Zn, and the components were α-magnesium and intermetallic MgZn. In the characterization of Scanning Electron Microscope (SEM) shows with increasing thickness of PCL layer up to ± 70μm, morphology effect on porosity that appear become smaller and rarer. Then in In-vitro test of Simulated Body Fluid (SBF) to calculate the degradation rate that the degradation rate decreased to 1.55 cm / year, while from the tape test adhesion, the strength of adhesion is increased to grade 4B according to ASTM D3995
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Uncontrolled Keywords: | Biodegradable, Magnesium Alloy, Polycaprolactone, Spray Coating |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA491 Metal coating. |
| Depositing User: | Nur Iskandar Muhammad |
| Date Deposited: | 24 Jun 2021 05:31 |
| Last Modified: | 24 Jun 2021 05:31 |
| URI: | http://repository.its.ac.id/id/eprint/54920 |