Pengaruh Penambahan V2O5-Bi2O3 terhadap Sintering dan Karakterisik Material Dielektrik Mg0,8Zn0,2TiO3

Avianti, Hilda (2018) Pengaruh Penambahan V2O5-Bi2O3 terhadap Sintering dan Karakterisik Material Dielektrik Mg0,8Zn0,2TiO3. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of Hilda A - 01111440000065.pdf]
Preview
Text
Hilda A - 01111440000065.pdf - Accepted Version

Download (2MB) | Preview

Abstract

Sintesis material 0,9MZT-xV2O5-yBi2O3 telah berhasil dilakukan dengan metode solid state reaction. Tujuan dari penelitian ini adalah untuk menurunkan temperature sintering Mg0.8Zn0.2TiO3 dari 1350oC menjadi 950oC dengan penambahan 10% V2O5-Bi2O3 serta mengetahui perubahan sifat dielektrik material Mg0.8Zn0.2TiO3. Variasi yang digunakan dalam penelitian ini adalah komposisi persen mol dari penambahan material V2O5 dan Bi2O3. Sintesis dilakukan dengan alat Atrittor rotary selama 6 jam dengan kecepatan 600 rpm. Sampel yang telah disintesis kemudian dikompaksi serta disinter pada temperatur 950oC. Sampel diuji dengan pengujian XRD, densitas, dan dielektrik. Penelitian ini menggunakan variasi komposisi molaritas untuk V2O5 yakni 3%, 5%, dan 7%. Dari pengujian tersebut diperoleh sampel yang paling bagus pada variasi 3%mol V2O5. Sampel tersebut memiliki 4 fasa yaitu fasa MZT, Bi4V1,5Ti0,5O10,85, Bi2Ti2O7, dan MgTi2O5 dengan hasil densitas relatif sebesar 99,16%. Rata-rata nilai permitivitas relatif (r) pada daerah dipol polarisasi variasi 3%mol V2O5 sebesar 22,751. Hasil ini lebih besar dibandingkan dengan variasi lainnya. Sehingga dari semua hasil penelitian yang diperoleh, material V2O5 dan Bi2O3 berhasil menurunkan temperatur sintering menjadi 950oC serta memperbaiki sifat listrik material dielektrik Mg0.8Zn0.2TiO3 ==================================================== The synthesis 0,9MZT-xV2O5-yBi2O3 material has been successfully performed by solid reaction method. The purpose of this research is to reduce sintering temperature of Mg0.8Zn0.2TiO3 from 1350oC to 950oC with V2O5-Bi2O3 addition and investigate the dielectric properties of Mg0.8Zn0.2TiO3. The variation used in this research is the composition of 10% percent mol V2O5-Bi2O3 addition. Synthesis was performed by means of rotary Atrittor for 6 hours with a speed of 600 rpm. The synthesized samples were then compressed and sintered at 950. Samples were tested with XRD, density, and dielectrical measurement. This final project use variation of molar presentage composition of V2O5 that are 3%, 5%, and 7%. From the test, the best samples were obtained at 3%mol V2O5. The sample has 3 phase ie MZT phase, Bi4V1,5Ti0,5O10,85, Bi2Ti2O7, and MgTi2O5 with the result of Relative density 99,16%. The relative permitivity at dipole polarization area of variation 3%mol V2O5 is 22,751. This result is bigger than the other variation. So from all the results obtained, V2O5 and Bi2O3 material managed to lower the sintering temperature to 950oC and possess excellent material dielectric Mg0.8Zn0.2TiO3

Item Type: Thesis (Undergraduate)
Subjects: Q Science > QC Physics > QC610.3 Electric conductivity
Divisions: Faculty of Natural Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User: Hilda Avianti
Date Deposited: 25 Jun 2021 10:18
Last Modified: 25 Jun 2021 10:18
URI: http://repository.its.ac.id/id/eprint/55335

Actions (login required)

View Item View Item