Pabrik Gypsum dari Kalsium Karbonat (CaCO3) dan Asam Sulfat (H2SO4) dengan Proses Sintesis

Apsari, Nuansa and Naafiumamah, Farihah (2018) Pabrik Gypsum dari Kalsium Karbonat (CaCO3) dan Asam Sulfat (H2SO4) dengan Proses Sintesis. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of PABRIK GYPSUM KITA.pdf]
Preview
Text
PABRIK GYPSUM KITA.pdf - Accepted Version

Download (1MB) | Preview

Abstract

Perkembangan pembangunan di Indonesia pada era globalisasi semakin meningkat dapat dibuktikan dengan semakin banyaknya proyek pembangunan fisik di seluruh nusantara baik di desa maupun kota. Dengan semakin meningkatnya pembangunan fisik di Indonesia, maka kebutuhan semen dan bahan bangunan lain seperti wallboard juga mengalami peningkatan. Peningkatan kebutuhan akan semen dan wallboard berdampak meningkatnya kebutuhan kalsium sulfat dihidrat (gypsum).
Gypsum dibuat dari proses sintesis. Pada proses ini, CaCO3 dimasukan kedalam mixer kemudian ditambahkan dengan H2O. Bahan baku cair berupa H2SO4 98% dimasukan kedalam mixer kemudian ditambahkan dengan H2O hingga menghasilkan H2SO4 50%. Kemudian CaCO3 direaksikan dengan asam sulfat (H2SO4) 50% di reaktor pada kondisi operasi suhu 93°C dan tekanan 1 atm. Konversi yang dihasilkan dengan metode ini sebesar 87,2%. Produk keluar reaktor berupa slurry kemudian kemudian dimasukkan ke dalam rotary vacuum filter untuk untuk dipisahkan cake dengan filtratnya. Produk cairan hasil filtrasi direcycle menuju reaktor. Cake gypsum dimasukan kedalam rotary dryer untuk dihilangkan kandungan airnya. Gypsum kemudian masuk ke silo sebagai tempat penyimpanan sebelum proses pengemasan. Kemurnian dari gypsum yang dihasilkan proses ini lebih dari 91%.
Pabrik gypsum dirancang dengan kapasitas 132.000 ton/tahun. Bahan baku yang digunakan adalah kalsium karbonat (CaCO3) dan asam sulfat (H2SO4). Pabrik ini direncanakan didirikan di Kecamatan Semanding, Kabupaten Tuban Jawa Timur pada tahun 2022. Pabrik Gypsum ini direncanakan beroperasi secara kontinyu selama 300 hari/tahun dengan basis 24 jam/hari.
Kata kunci: gypsum, kalsium karbonate, asam sulfat, sintesis
=========================================================
Development of industrial in Indonesia in globalization era was increasingly evidenced by the increasing number of physical development projects throughout the archipelago, both in rural and urban areas. With the increasing physical development in Indonesia, the need for cement and other building materials such as wallboard also increased. Increasing the need for cement and wallboard impacts the need for calcium sulfate dihydrate (gypsum).
Gypsum is made from synthesis process. In this process, CaCO3 is added to the mixer then added with H2O. The liquid raw material of H2SO4 98% is fed into the mixer and then added with H2O to produce 50% H2SO4. Then CaCO3 was reacted with 50% sulfuric acid (H2SO4) in the reactor under operating conditions of 93 ° C and 1 atm pressure. The conversion generated by this method is 87.2%. The reactor exit product is slurry and then put into the rotary vacuum filter to separate the cake with the filtrate. The product of filtration fluid is recycled to the reactor. The gypsum cake is put into the rotary dryer to remove the water content. Gypsum then enter the silo as a storage place before the packing process. The purity of the gypsum produced by this process is more than 91%.
Gypsum factory is designed with a capacity of 132,000 tons / year. The raw material used is calcium carbonate (CaCO3) and sulfuric acid (H2SO4). This plant is planned to be established in Semanding Subdistrict, Tuban Regency, East Java in 2022. This Gypsum Plant is planned to operate continuously for 300 days / year on a 24 hour / day basis.
Keywords : gypsum, calcium carbonate, sulfuric acid, synthesis

Item Type: Thesis (Diploma)
Uncontrolled Keywords: gypsum, kalsium karbonate, asam sulfat, sintesis
Subjects: T Technology > T Technology (General) > T58.5 Information technology. IT--Auditing
Divisions: Faculty of Vocational > 24305-Industrial Chemical Engineering Technology
Depositing User: Nuansa Apsari
Date Deposited: 28 Jun 2021 03:09
Last Modified: 28 Jun 2021 03:09
URI: http://repository.its.ac.id/id/eprint/55487

Actions (login required)

View Item View Item