Sintesis Al-UiO-66 Dengan Penambahan Modulator Asam Asetat dan Aktivitasnya sebagai Katalis pada Reaksi Esterifikasi Asam Oleat

Widiawati, Oktavia Clara (2018) Sintesis Al-UiO-66 Dengan Penambahan Modulator Asam Asetat dan Aktivitasnya sebagai Katalis pada Reaksi Esterifikasi Asam Oleat. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 01211440000011-Undergraduate_Theses.pdf]
Preview
Text
01211440000011-Undergraduate_Theses.pdf - Accepted Version

Download (2MB) | Preview

Abstract

Padatan UiO-66 dan Al-UiO-66 telah berhasil disintesis dengan metode solvotermal dalam pelarut N-N’-dimetilformamida (DMF) pada suhu 120 °C selama 24 jam dengan penambahan modulator asam asetat. Variasi perbandingan mol Al2O3 terhadap ZrCl4 sebesar 0,3 dan 0,5, Padatan yang dihasilkan berturut-turut dinotasikan sebagai UiO-66, UiO-66-Ac, Al(0,5)-UiO-66, Al(0,3)-UiO-66, Al(0,5)-UiO-66-Ac, Al(0,3)-UiO-66-Ac. Pola difraktogram padatan hasil sintesis menunjukkan puncak karakteristik pada 2θ sebesar 7,4° dan 8,5° yang merupakan puncak karakteristik dari UiO-66 standar. Spektra FTIR padatan hasil sintesis menunjukkan pita serapan pada bilangan gelombang sekitar 1550-1630 dan 1450-1580 cm-1, serta pita serapan kuat pada 1400 cm-1, yang merupakan pita serapan karakteristik UiO-66 standar. Padatan Al(0,5)-UiO-66 dan Al(0,5)-UiO-66-Ac berturut-turut memiliki stabilitas termal pada suhu mencapai 540 °C dan 545 °C. Hasil pengujian aktivitas Al(0,5)-UiO-66 sebagai katalis pada reaksi esterifikasi asam oleat menunjukkan konversi sebesar 91,2%, lebih rendah dari Al(0,5)-UiO-66-Ac (94,5%). Nilai konversi tertinggi adalah 97,8% pada penggunaan katalis UiO-66-Ac.
=======================================================================================================
UiO-66, UiO-66-Ac, Al-UiO-66 and Al-UiO-66-Ac have been synthesized by solvotermal method using N-N'-dimethylformamide (DMF) as solvent at 120 ° C for 24 hours. The amount variation of Al2O3 to ZrCl4 was 0,3 and 0,5 mmol, and the acetic acid modulator used was 17,1 mL (1: 100). The resulting solids are respectively denoted as UiO-66, UiO-66-Ac, Al(0,5)-UiO-66, Al(0,3)-UiO-66, Al(0,5)-UiO-66-Ac, Al(0,3)-UiO-66-Ac. The solid synthesis diffractogram pattern shows the characteristic peak at 2θ of 7,3 ° and 8,5 ° which is the characteristic peak of the standard UiO-66. The solid-state synthesis FTIR spectra exhibited absorption bands at wave numbers of about 1550-1630 and 1450-1580 cm-1, as well as a strong absorption band at 1400 cm-1, which is the standard UiO-66 characteristic. Al(0,5)-UiO-66 and Al(0,5)-UiO-66-Ac have successively stable at temperatures reaching 540 ° C and 545 ° C. The results of Al(0,5)-UiO-66 activities as catalyst at esterification of oleic acid showed conversion of 91,2%, lower than Al(0,5)-UiO-66-Ac (94,5%). The highest conversion of 97,8% on the use of UiO-66-Ac catalyst.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 660.284 4 Wid s-1 3100018077543
Uncontrolled Keywords: UiO-66, Al-UiO-66, Modulator, Asam asetat, Katalis, Esterifikasi, Asam Oleat
Subjects: Q Science > QD Chemistry
Q Science > QD Chemistry > QD305.A2 O73 Esterification
Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions: Faculty of Natural Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Oktavia Clara Widiawati
Date Deposited: 01 Dec 2020 09:17
Last Modified: 01 Dec 2020 09:17
URI: http://repository.its.ac.id/id/eprint/55616