Elsandika, Gabriela (2018) Sintesis dan Karakterisasi Keramik Zirkon dengan Penambahan Sintering Agent. Masters thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
01111650010008-Master_Thesis.pdf - Accepted Version Download (3MB) | Preview |
Abstract
Sintesis keramik padat ZrSiO4 menggunakan bahan dasar serbuk zirkon
hasil ekstraksi dari pasir alam yang berasal dari Kereng Pangi Kalimantan Tengah
telah selesai dilakukan. Keramik zirkon disintesis dengan dan tanpa penambahan
sintering agent berupa B2O3 (ZB), V2O5 (ZV), dan Bi2O3 (ZBi) sebesar 3,6, dan 9
wt.%. Sintesis dilakukan pada temperatur 1100, 1200, 1300 °C dengan waktu
penahanan selama lima jam.
Karakterisasi fasa dilakukan dengan XRD, kemudian dianalisis secara
kualitatif dan kuantitatif. Identifikasi fasa menunjukkan fasa tunggal zirkon untuk
keramik Z0, ZB, ZV di semua temperatur. Sedangkan identifikasi fasa untuk
keramik ZBi menunjukkan fasa tunggal pada temperatur 1100 dan 1200 °C.
Selain itu, teridentifikasi fasa zirkon dan zirkonia tetragonal pada temperatur 1300
°C.
Nilai densitas keramik diuji dengan densimeter elektronik. Sedangkan
nilai kekerasan keramik diukur dengan microhardness Vickers. Dari hasil tersebut
dapat ditentukan bahwa B2O3 merupakan sintering agent yang paling efektif
untuk menghasilkan keramik zirkon dengan densitas relatif 90,97% dan
kekerasan 2,26 GPa. Jumlah yang dibutuhkan adalah 6 wt.% dengan temperatur
sinter 1300 °C. Uji SEM menampilkan bentuk mikrografi keramik keramik ZB6
1300 paling rapat dibanding yang lain.
========================================================================================================
Synthesis of ZrSiO4 ceramics using the raw material from the extraction
zircon of Kereng Pangi Central Kalimantan natural sand has been completed.
Zircon ceramics are synthesized with and without 3.6, and 9 wt.% sintering agents
addition i.e. B2O3 (ZB), V2O5 (ZV), and Bi2O3 (ZBi). The synthesis was carried
out at a temperature of 1100, 1200, 1300 ° C with a five-hour holding time.
Phase characterization was done with XRD, then analyzed qualitatively
and quantitatively. The phase identification shows a single zircon phase for
ceramics Z0, ZB, ZV at all temperatures. While the phase identification for ZBi
ceramics shows a single phase at temperatures of 1100 and 1200 ° C. In addition,
zircon and zirconia tetragonal phase were identified at 1300 ° C.
The value of ceramic density was tested by electronic densimeter. While
the value of ceramics hardness is measured by Vickers microhardness. From these
results can be determined that B2O3 is the most effective sintering agent to
produce zircon ceramics with 90.97% relative density and 2,26 GPa hardness. The
required amount of B2O3 is 6 wt.%, with a sinter temperature 1300 ° C. The SEM
characterization shows ZB6 1300 ceramics grain form most closely than others.
| Item Type: | Thesis (Masters) |
|---|---|
| Additional Information: | RTFi 553.61 Els s-1 3100018078322 |
| Uncontrolled Keywords: | pasir zirkon, keramik zirkon, B2O3, V2O5, Bi2O3, zircon sand, zircon ceramics |
| Subjects: | Q Science > QC Physics Q Science > QD Chemistry > QD251.2 Chemistry, Organic. Biochemistry Q Science > QE Geology > QE391.Z7 Zircon |
| Divisions: | Faculty of Natural Science > Physics > 45101-(S2) Master Thesis |
| Depositing User: | Gabriela Elsandika |
| Date Deposited: | 18 Jan 2019 06:16 |
| Last Modified: | 09 Feb 2021 08:30 |
| URI: | http://repository.its.ac.id/id/eprint/55669 |