Pengaruh Variasi Filler ER70S-6 dan E71T-1C pada Pengelasan Baja SA-36 Menggunakan Metode Pengelasan GMAW dan FCAW

Arga, Ely Stya (2018) Pengaruh Variasi Filler ER70S-6 dan E71T-1C pada Pengelasan Baja SA-36 Menggunakan Metode Pengelasan GMAW dan FCAW. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10211500000115_Non_Degree.pdf]
Preview
Text
10211500000115_Non_Degree.pdf - Accepted Version

Download (3MB) | Preview

Abstract

Pada waktu ini proses pengelasan dipergunakan dalam pelaksanaan kontruksi bangunan baja, kontruksi mesin dan lain sebagainya. Proses pengelasan harus benar-benar memperhatikan kesesuaian antara sifat-sifat las dan sifat material yang akan di las. Materialnya ASTM A36 untuk mengetahui hasil pengelasan dengan variasi filler terhadap kekerasan,struktur mikro dan kekuatan tarik.
Penelitian ini menggunakan metode eksperimen untuk mengetahui perbedaan pengelasan dengan variasi filler ER70S-6 dan E71T-1C terhadapa hasil lasan. Pengujian dilakukan di Workshop Jurusan Teknik Mesin Industri FV-ITS Surabaya. Parameter yang diamati dalam penelitian ini adalah uji kekerasan, uji metalografi, dan uji Tarik.
Dari hasil pengujian dapat diperoleh hasil pada filler ER70S-6 nilai kekerasan tertinggi pada area logam las sebesar 86,6 dan kekuatan tarik sebesar 2300.66 kgf dikarenakan cacat IP (incomplete penetration) pada hasil las an, sedangkan pada filler E71T-1C dengan cara pengelasan backweld memiliki nilai kekerasan tinggi pada area HAZ sebesar 83,3 dan kekuatan tarik sebesar 4221.69 kgf
===================================================================================================
At this time the welding process is used in the implementation of construction steel buildings, construction machinery and each other. The welding process should really pay attention to the suitability between the welding properties and the material properties to be welded. The material is ASTM A36 to know the welding result with filler variation to hardness test, micro structure test and tensile strength test.
This research uses experimental method to know the difference of welding result with filler variation ER70S-6 and E71T-1C. The test was conducted in Workshop of Industrial Engineering Department of FV-ITS Surabaya. The parameters observed in this research are hardness test, metallographic test, and tensile strength test.
From the test results can be obtained results on the filler ER70S-6 has highest hardness value at the weld metal area of 86.6 and tensile strength amount 2300.66 N / mm2 caused incomplete penteration defflected, while the E71T-1C filler with backweld metode has high hardness value in the HAZ area of 83.3 and tensile strength amount 4221.69 kgf.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Las FCAW , Filler AWS A5.18 ER70S-6, Filler E71T-1C
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TA Engineering (General). Civil engineering (General) > TA492.W4 Welded joints
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Ely Stya Arga
Date Deposited: 09 Aug 2021 20:48
Last Modified: 09 Aug 2021 20:48
URI: http://repository.its.ac.id/id/eprint/58911

Actions (login required)

View Item View Item