Pengaruh Variasi Besarnya Arus Terhadap Nilai Kekerasan Permukaan Dan Lebar HAZ Pada Proses Pemotongan Baja SS 400 Menggunakan Elektroda Carbon Gouging Diameter 6MM

Noya, Abri Denny (2018) Pengaruh Variasi Besarnya Arus Terhadap Nilai Kekerasan Permukaan Dan Lebar HAZ Pada Proses Pemotongan Baja SS 400 Menggunakan Elektroda Carbon Gouging Diameter 6MM. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10211500000080-Abri Denny Noya.pdf]
Preview
Text
10211500000080-Abri Denny Noya.pdf - Accepted Version

Download (4MB) | Preview

Abstract

Pemotongan Logam menggunakan proses las dengan elektroda carbon gouging dipergunakan dalam konstruksi bangunan, dikarnakan proses ini lebih efisien dalam penggunaannya maka pada proses pemotongan ini haruslah diperhatikan sifat-sifat benda dan cara-carapemotongan berdasarkan fungsi dan tujuan.
pada penelitian ini adalah pemotongan menggunakan metode elektroda carbon gouging dengan variasi besarnya arus listrik yang dipakai terhadap baja SS400. variasibesarnya arus yang digunkan adalah 260A, 280A, dan 300A. Kemudian diuji kekasaran permukaan dan makro ETSA
Pada hasil pengujian kekasaran permukaan, permukaan yang paling halus terdapat pada arus 280A untuk hasil pengamatan Makro ETSA didapatkan lebar HAZ yang terbesar terdapat pada hasil pemotongan menggunakan arus 300A dan yang terkecil menggunakan 260. Pada pengamatan ini didapatkan arus yang terbaik sebesar 280A dikarnakan mempunyai kekasaran permukaan yang halus meskipun mempunyai lebar HAZ yang sedikit lebih lebar
==================================================================================================================
Cutting of metal with welding process using a carbon
gouging electrode is often used in building constructions, this
cutting process is more efficient, which is needs to be handled
with care and looked upon based on the function and point of the
cutting process.
This observation is cutting process using carbon gouging
electrode with electricity current variation for mild steel SS400.
The electricity current variations are 260 A, 280 A and 300 A.
and then uses toughness testings and metallography by using a
way called macro ETSA.
On this observation, thoughness surface, the smoothest
surface is on current 280 A. from macro ETSA testing, the widest
HAZ area is on current 300 A and the narrowest HAZ area is on
current 260 A. From this observation is we got the best electricity
current is 260 A because having the smoothest toughness surface,
although the HAZ area is the widest from all.

Item Type: Thesis (Diploma)
Additional Information: RSMI 671.53 Noy p
Uncontrolled Keywords: Ampere, Carbon Gouging, Foto Makro, Kekasaran
Subjects: T Technology > TS Manufactures > TS227 Welding.
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Abri Denny Noya
Date Deposited: 03 Nov 2020 07:18
Last Modified: 03 Nov 2020 07:18
URI: http://repository.its.ac.id/id/eprint/59267