Studi Pengaruh Root Gap Terhadap Sifat Mekanik Dan Struktur Mikro Pada Sambungan Las Pelat ASTM A36

Fahmy, Randistya (2015) Studi Pengaruh Root Gap Terhadap Sifat Mekanik Dan Struktur Mikro Pada Sambungan Las Pelat ASTM A36. Undergraduate thesis, Institut Technology Sepuluh Nopember.

[img]
Preview
Text
4110100031-Undergraduate Thesis.pdf - Published Version

Download (6MB) | Preview

Abstract

Pengelasan SMAW (Shielded Metal Arc Welding) mempunyai aplikasi luas di dalam dunia industri. Untuk penguasaan teknologi pengelasan maka perlu dilakukan penelitian lanjut tentang pengaruh gap terhadap struktur mikro setelah mengalami pengelasan. Pengelasan sendiri adalah suatu proses penyambungan logam dengan logam menjadi satu akibat adanya panas, sehingga dalam prosesnya akan dapat mengubah sifat dasar dari material dasar (based material). Pada penelitian ini, variable yang digunakan adalah baja karbon ASTM A36. Setelah dilakukan pengelasan dengan variable yang sudah ditentukan dan batasan-batasan masalah selama penelitian. Selanjutnya dilihat nilai uji kekerasan (hardness) dan uji struktur mikro. Sepesimen hasil pengelasan yang dibutuhkan sebanyak 3 buah dengan tebal 12mm. Specimen tersebut diberi variasi kampuh las single-V groove dengan sudut 60° dan variasi gap yaitu 2mm, 4mm, dan 5mm pada kampuh las logam induk baja karbon ASTM A36. Hasil pengujian menunjukkan bahwa pengelasan yang dilakukan adalah baik. Spesimen dengan variasi lebar root 3 mm, 4 mm, dan 5 mm menghasilkan lebar HAZ rata-rata yang berturut turut mengalami kenaikan. Lebar HAZ berkisar antara 1 mm sampai 2.5 mm. Harga kekerasan rata-rata pada daerah HAZ dan weld metal menunjukkan bahwa pada spesimen variasi root gap 3 mm mempunyai kekerasan sebesar 176.57 HV dan 179.93 HV yang lebih rendah daripada spesimen dengan variasi root gap 4 mm sebesar 180.23 HV dan 183.57 HV. Sedangkan untuk variasi root gap 5 mm sebesar 182.13 HV dan 186.33 HV. Dari percobaan tersebut diketahui bahwa pengaruh memperlebar root gap dapat mempengaruhi sifat mekanik dan struktur mikro hasil las. Semakin keras nilai suatu material maka material tersebut memiliki sifat getas. ======================================================================================================== SMAW (Shielded Metal Arc Welding) has broad application in the industry. For welding technology mastery is necessary to do further research on the effect of the gap againts microstructure after welding. Welding is a process of joining metals due to the heat, until the process will be able to change the material properties. In this research, the variables used carbon steel ASTM A36. After welding process with predifined variables and limitations problem during the research, furthermore obtained hardness value and its microstructure. The results of specimens after welding process are three pieces of specimens required with a thickness 1 - and 5 mm on the base metal seam weld ASTM A36 carbon steel. The results show that well result of welding process. Specimens with root gap 3 mm, 4 mm, and 5 mm variations produces width of HAZ is evenly succesive increase. HAZ width ranging from 1 mm to 2.5 mm. Hardness value in the HAZ and weld metal region indicates that the specimens variation in root gap 3 mm has a hardness value 176.57 HV and 179.93 HV that lower than the specimens with variation of the root gap 4 mm with hardness value 180.23 HV and 183.57 HV. Whereas for the variation in the root gap 5 mm with hardness value at 182.13 HV and 186.33 HV. The results of the experiment are known that the effect of widening the root gap can affect the mechanical properties and microstructure at welds metal and HAZ. More increasingly hardness value of the materials, the materials has a brittle properties

Item Type: Thesis (Undergraduate)
Additional Information: RSPe 623.843 2 Fah s
Uncontrolled Keywords: A36, Root gap, SMAW, Struktur Mikro, Hardness
Subjects: V Naval Science > VM Naval architecture. Shipbuilding. Marine engineering
Divisions: Faculty of Marine Technology > Naval Architecture and Shipbuilding Engineering > (S1) Undergraduate Theses
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 19 Sep 2018 08:06
Last Modified: 19 Sep 2018 08:06
URI: http://repository.its.ac.id/id/eprint/59679

Actions (login required)

View Item View Item