Fabrikasi Lapisan Tio2 Dengan Metode Spin Coating Dan Karakterisasi Sifat Optik Serta Aktivitas Fotokatalisnya

Zharvan, Vicran (2015) Fabrikasi Lapisan Tio2 Dengan Metode Spin Coating Dan Karakterisasi Sifat Optik Serta Aktivitas Fotokatalisnya. Masters thesis, Institut Technology Sepuluh Nopember.

[img] Text
1113201013-Master Thesis.pdf - Published Version
Restricted to Repository staff only

Download (2MB) | Request a copy

Abstract

Telah disintesis partikel nano TiO2 dengan menggunakan metode kopresipitasi menggunakan prekursor TiCl3 dengan memvariasikan lama waktu pengadukan selama 5 jam, 10 jam dan 25 jam. Fabrikasi lapisan TiO2 dilakukan dengan melarutkan serbuk nano TiO2 ke dalam terpineol dan ethylcellulose kemudian dilapiskan ke substrat kaca corning dengan menggunakan metode spincoating. Lapisan yang telah difabrikasi selanjutnya dikarakterisasi morfologi menggunakan SEM, identifikasi fasa menggunakan XRD dan sifat optik menggunakan UV-Vis spektroskopi. Pengujian aktivitas fotokatalis lapisan TiO2 dilakukan dengan mengamati fotodegradasi polutan metilen biru 12 ppm selama 5 jam penyinaran menggunakan lampu UV. Hasil penelitian menunjukkan serbuk nano TiO2 yang disintesis memiliki ukuran kristal 9,6 nm-11,8 nm dengan fasa anatase. Daerah penyerapan lapisan TiO2 berada dalam rentang panjang gelombang UV serta lapisan dengan serbuk TiO2 pengadukan 5 jam memiliki aktivitas fotokatalis yang baik. ==================================================================================================== Nano-sized TiO2 particles have successfully been synthesized by coprecipitation method using TiCl3 as a precursor and varying mixing time for 5 hours, 10 hours and 25 hours. The TiO2 film was prepared by dissolved TiO2 nanopowder into terpineol and ethylcellulose then coated onto corning glass using spin coating method. The films were then checked using SEM, XRD and UV-Vis to obtain their morphology, phase and optical properties. The photocatalytic measurement of TiO2 films were conducted by photodegradation of 12 ppm methylene blue solution for 5 hours irradiation using UV lamp. Result shows that all of TiO2 powders have anatase phase with crystalline size in the range of 9,6 nm – 11,8 nm. The TiO2 films have absorbance region near UV range. The film containing TiO2 particles prepared with stirring period for 5 hours has the best photocatalytic activity.

Item Type: Thesis (Masters)
Additional Information: RTFi 620.118 Zha f
Uncontrolled Keywords: TiO2, fotokatalis, SEM, XRD, UV-Vis
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials
Divisions: Faculty of Mathematics and Science > Physics > (S2) Master Theses
Depositing User: Mr. Tondo Indra Nyata
Date Deposited: 12 Nov 2018 03:15
Last Modified: 12 Nov 2018 03:15
URI: http://repository.its.ac.id/id/eprint/59953