Studi Eksperimen Pengaruh Perbedaan Filler Metal Er309 Dan ERNiCr-3 Terhadap Komposisi Kimia Sambungan Las Dissimilar Metal Antara Austenitic Stainless Steel SS347HTB Dan Low Alloy Steel T91 Dengan Proses GTAW

Yorgie, Yorgie (2019) Studi Eksperimen Pengaruh Perbedaan Filler Metal Er309 Dan ERNiCr-3 Terhadap Komposisi Kimia Sambungan Las Dissimilar Metal Antara Austenitic Stainless Steel SS347HTB Dan Low Alloy Steel T91 Dengan Proses GTAW. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 2115105045 - Undergraduate_Theses.pdf - Accepted Version Restricted to Repository staff only until 1 October 2023. Download (4MB) | Request a copy

Abstract

Dissimilar metal welding (DMW) merupakan salah satu metode untuk menyambungkan logam yang berbeda contohnya seperti penyambungan stainless steel (SS) dengan baja paduan karbon rendah. Sambungan kedua jenis logam tersebut umumnya digunakan pada pembangkit listrik khususnya pada bagian tube boiler. Hal ini dikarenakan tube boiler bekerja pada suhu dan tekanan berbeda sehingga akan mempengaruhi penggunaan material yang digunakan. Umumnya pada bagian suhu tinggi terbuat dari baja tahan karat austenite yang memiliki sifat tahan karat yang sangat baik pada suhu dan tekanan tinggi, dan pada bagian dengan suhu lebih rendah digunakan baja paduan dikarenakan nilai keekonomisan dari material tersebut. Namun pada DMW terdapat kekurangan dimana akibat perbedaan komposisi kimia antara material yang terjadi pada sepanjang garis fusi mengakibatkan sifat mekanik dan struktur mikro berbeda sehingga sambungan akan rentan terhadap kegagalan. Salah satu langkah dalam mengurangi permasalah yang terdapat pada DMW adalah dengan memprediksi kandungan komposisi kimia pada weld metal dimana komposisi kimia dapat diatur dengan cara pemilihan kawat las yang benar sesuai dengan standar yang digunakan
Dalam penelitian ini dilakukan pengelasan dissimilar metal antara SS347HTB dan low alloy carbon steel (T91) dengan variasi filler metal ER309 dan ERNiCr-3, dimana voltase dan arus pengelasan sama. Variasi pengelasan ini menggunakan metode gas tungsten arc welding (GTAW). Setelah dilakukan proses pengelasan dilakukan pengujian merusak ,pengujian metalurgi dan pengujian SEM-EDS. Pengujian yang dilakukan dalam penelitian ini adalah pengujian kekerasan dengan microvickers, pengujian metallography serta pengujian kandungan delta ferrite dan pengujian Scanning Electron Microscope (SEM).
Dari pengujian tersebut diketahui struktur mikro, komposisi kimia logam las dan distribusi kekerasan. Hasil pengujian kekerasan pada spesimen yang menggunakan kawat ERNiCr-3 nilai tertinggi ada pada bagian logam las dan pada spesimen yang menggunakan kawat ER309 nilai kekerasan tertinggi ada pada bagian HAZ T91. Pada struktrur mikro kedua spesimen dengan dua kawat las terbentuk presipitasi karbida kromium dengan jumlah yang kecil.
================================================================================================
Dissimilar metal welding (DMW) is one method for connecting different metals, for example, as stainless steel (SS) connectors with low carbon alloy steel. This type of metal kettle is usually used in special power plants in the boiler tube section. This is because boiler tubes work at different temperatures and pressures that will affect the use of the materials used. Austenite which has excellent corrosion resistance at high temperatures and pressures, and in parts with higher temperatures used alloy steel with the economic value of the material. However, in DMW, there is a difference between the chemical composition of the material that occurs in the fusion line, which is caused by different mechanical and microstructure so that it will be susceptible to change. One of the steps in reducing the problems needed in DMW is to predict the chemical composition of welding metals where the chemical composition can be regulated by selecting welding wires that are really in accordance with the standards used
In this study different metals were welded between SS347HTB and low alloy carbon steel (T91) with variations in filler metal ER309 and ERNiCr-3, where the voltage and current of welding were the same. This welding variation uses the arc welding tungsten gas method (GTAW). After the welding process is carried out damage testing, metallurgical testing and SEM-EDS testing. Tests carried out in this study were hardness testing with microvickers, metallographic testing and ferrite delta testing and Scanning Electron Microscope (SEM) testing.
From these tests it is known microstructure, chemical composition of weld metal and hardness distribution. Test results on specimens using the highest value ERNiCr-3 wire on weld metal parts and on specimens using ER309 wire the highest hardness value on the HAZ T91 section. In the second specimen microstructure with two welding wires, small amounts of chromium carbide are formed.

Item Type:	Thesis (Undergraduate)
Additional Information:	RSM 671.52 Yor s-1 2019
Uncontrolled Keywords:	Dissimilar metal welding; ER309; ENiCr-3; GTAW; asutenitic stainless steel 347HTB, low alloy steel T91; SEM
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TN Mining engineering. Metallurgy T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy T Technology > TN Mining engineering. Metallurgy > TN879.6 Welding
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Yorgie .
Date Deposited:	09 Nov 2021 06:57
Last Modified:	09 Nov 2021 06:57
URI:	http://repository.its.ac.id/id/eprint/61427

Actions (login required)

View Item