Pengaruh Overlap Ratio Dan Ukuran Grit Silicon Carbide Wheel Grinder Terhadap Amplitudo Getaran Dan Kekasaran Permukaan Untuk Material OCR12VM

Putra, Fachrizal Cesar Putra (2019) Pengaruh Overlap Ratio Dan Ukuran Grit Silicon Carbide Wheel Grinder Terhadap Amplitudo Getaran Dan Kekasaran Permukaan Untuk Material OCR12VM. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 02111650010002-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2022. Download (15MB) | Request a copy

Abstract

Dewasa ini pemakaian mesin perkakas tak bisa dipisahkan dari kehidupan manusia dalam proses produksi. Proses produksi part suatu alat atau mesin dibutuhkan kualitas dan kepresisian yang tinggi untuk memenuhi permintaan dan bersaing di pasaran. Salah satu dari mesin perkakas yang dapat menentukan kualitas dan kepresisian pada hasil produksi adalah gerinda. Proses gerinda adalah proses finishing dari proses pemesinan yang bertujuan untuk menghasilkan permukaan benda kerja yang halus bahkan dapat mengerjakan benda kerja dengan tuntutan ukuran yang sangat presisi. Pemilihan batu gerinda yang tepat dalam proses pemesinan juga merupakan salah satu faktor penentu keberhasilan pengerjaan benda kerja. Silicon carbide merupakan salah satu jenis batu gerinda yang digunakan untuk menggerinda benda kerja. Bahan asah ini dibuat dari pasir silika dan arang batu. Ukuran grit juga menjadi salah satu faktor yang mempengaruhi kualitas kekasaran permukaan. Selain dari pemilihan batu gerinda beserta ukuran gritnya, proses pemesinan yang baik harus menghindari beberapa faktor salah satunya getaran dikarenakan getaran dapat menurunkan kualitas hasil produksi baik kualitas permukaan benda kerja maupun tingkat kepresisian benda kerja. Salah satu kerugian terbesar dari adanya getaran dalam proses pemesinan yaitu dapat menyebabkan pahat mudah aus, patah bahkan mengakibatkan kerusakan pada mesin. Dari latar belakang tersebut, tesis ini mengangkat tentang pengaruh ukuran grit silicon carbide wheel grinder terhadap respon getaran dan kekasaran permukaan material hardened tool steel OCR12VM pada proses grinding.

Penelitian ini terdiri dari beberapa tahapan, mulai dari studi literatur, identifikasi dan perumusan masalah, pengambilan data kekerasan permukaan dan respon getaran, serta pengolahan data menggunakan perangkat lunak. Material pengujian menggunakan hardened tool steel OCR12VM berukuran 300 x 60 x 20 (mm). Pengujian dilakukan menggunakan mesin surface grinding KGS818AH dengan variabel proses ukuran grit batu gerinda, putaran spindel, kedalaman potong, kecepatan makan, serta overlap ratio.

Pada penelitian ini bertujuan mengetahui seberapa besar pengaruh overlap ratio dan ukuran grit batu gerinda silicon carbide terhadap besarnya amplitudo getaran dan nilai kekasaran permukaan yang terjadi saat proses permesinan serta hubungan antara amplitudo getaran dan kekasaran permukaan.

Kesimpulan dari penelitian ini adalah seiring meningkatnya overlap ratio maka amplitudo getaran dan kekasaran permukaan akan menurun dan semakin halus grit batu gerinda maka amplitudo getaran dan kekasaran permukaan yang didapat akan lebih rendah serta terdapat korelasi antara amplitudo getaran terhadap kekasaran permukaan.
================================================================================================
Nowadays the use machine tools could not be separated from the human life in the process of production. Production process is part of a tool or machine required a high-precision and high quality to meet the demand and compete in the market. One of the machine tool that can determine the high quality and high accuracy on the results of the production was grinding. The process of grinding is a finishing process of the machining process that aims to produce a smooth workpiece surface can even work on the workpiece with the demands of a very precise size. The selection of the wheel grinding in the process of machining is also one of the deciding factors for the success of the workpiece. Silicon carbide is one of the types of wheel grinder used for grinding the workpiece. Test material is made from silica sand and coal. The grit size is also one of the factors that affect the quality of surface roughness. Aside from the selection of the wheel grinder with a grit size, good machining process must avoid several factors one of them of vibrations can decrease the quality of the production and quality of the surface roughness even workpiece precision. One of the largest losses of vibration in machining processes, namely the easy wear tool, broken even resulted in damage to the machine. From such a background, this thesis raised about the effect of overlap ratio and grit size silicon carbide wheel grinder on vibration amplitude and surface roughness for materials hardened tool steel OCR12VM on the process of grinding.
This research consists of several stages, ranging from the study of literature, problem identification, measurement vibration amplitude and surface roughness, and processing data with software. Testing material using hardened tool steel OCR12VM size 300 x 60 x 20 (mm). Testing using the surface grinding machine KGS818AH with variable process grit size wheel grinder, spindle speed, depth of cut, longitudinal feed, and overlap ratio.
On this research aims to find out how big the influence of overlap ratio and grit size silicon carbide wheel grinder to the vibration amplitude and surface roughness when grinding process and the corelation between the vibration amplitude and surface roughness.
The conclusion of this study is with increasing overlap ratio, the vibration amplitude and surface roughness will decrease and the finer the grit size silicon carbide wheel grinder, the vibration amplitude and surface roughness will be lower and there is a correlation between the vibration amplitude against surface roughness.

Item Type:	Thesis (Masters)
Additional Information:	RTM 671.35 Put p-1 2019
Uncontrolled Keywords:	Silicon carbide wheel grinder, overlap ratio, ukuran grit batu gerinda, amplitudo getaran, kekasaran permukaan.
Subjects:	Q Science > Q Science (General) > Q180.55.M38 Mathematical models Q Science > QA Mathematics > QA278.2 Regression Analysis. Logistic regression Q Science > QA Mathematics > QA935 Vibration
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21101-(S2) Master Thesis
Depositing User:	Fachrizal Cesar Putra
Date Deposited:	14 Dec 2021 01:46
Last Modified:	14 Dec 2021 01:46
URI:	http://repository.its.ac.id/id/eprint/61698

Actions (login required)

View Item