Putranto, Redhian Yoga (2019) Analisa Kerusakan Grab WireRope pada Ship Unloader Batu Bara. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02111645000062-Undergraduate_Thesis.pdf - Accepted Version Download (3MB) | Preview |
Abstract
Pembangkit Listrik Tenaga Uap (PLTU) merupakan sumber penghasil listrik yang utama di Indonesia, dengan menggunakan batu bara sebagai bahan bakarnya. Ship unloader merupakan salah satu peralatan pengangkut yang memegang peranan penting pada coal handling system, yang berfungsi untuk memindahkan batu bara dari kapal menuju conveyor menggunakan grab. Kerusakan pada ship unloader dapat menghambat proses pemindahan batu bara dari kapal ke stock pile. Salah satu komponen vital pada ship unloader adalah tali baja (wire rope). Tali baja (wire rope) memiliki masa pakai yang terbatas dan kemampuannya berkurang seiring berjalannya waktu karena pemakaian yang terus menerus. Faktor instalasi, cara penggunaan, dan perawatan yang dilakukan akan mempengaruhi masa pakai tali baja. Tali baja yang dibahas pada tugas akhir ini adalah tali baja pada bagian grab.
Analisa kerusakan grab wire rope ship unloader yang dilakukan adalah dengan melakukan analisa perhitungan tegangan yang diterima oleh wire rope karena beban operasi, kemudian menghitung perkiraan umur dari wire rope. Pengamatan maksrosopis dilakukan untuk mengetahui bentuk patahan yang terjadi pada tiap wire, bentuk patahan wire dapat merepresentasikan penyebab patahnya wire tersebut.
Hasil yang didapatkan dari analisa perhitungan beban yang diterima wire rope menunjukkan bahwa beban yang diterima selama wire rope beroperasi tidak melebihi beban ijinnya, sehingga wire rope aman untuk digunakan. Hasil dari pengamatan makro bentuk patahan menunjukkan bahwa jenis kerusakan kawat didominasi oleh kerusakan fatigue, dengan presentase sebesar 88,46%, tidak ditemukan cacat berupa korosi.
================================================================================================
Steam Power Plant (PLTU) is the main source of electricity in Indonesia, using coal as fuel. Ship unloader is one of the transportation equipment that plays an important role in coal handling system, which serves to move coal from ship to conveyor using grab. Damage to the ship unloader can inhibit the process of moving coal from ship to stock pile. One of the vital components of the ship unloader is a steel wire rope. Steel wire ropes have a limited lifetime and their ability to decrease over time due to continuous usage. The installation factor, how to use it, and the treatment performed will affect the life of the steel wire rope. The steel wire rope discussed in this final project is a steel wire rope on the grab section.
The failure analysis of the grab wire rope ship unloader is done by analyzing the calculation of the stress received by the wire rope due to the operating load, then calculating the approximate age of the wire rope. Macroscopic examination is done to determine the fracture that occurs on each wire, the wire fracture form can represent the cause of the broken wire.
The results obtained from the load calculation analysis received by the wire rope indicate that the load received during the wire rope operate does not exceed the load permit, so the wire rope is safe to use. The result of fracture macroscopic examination showed that the type of wire damage was dominated by fatigue damage, with a percentage of 88.46%, there are no corossion defects found on wire rope.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSM 621.402 Put a-1 2018 |
| Uncontrolled Keywords: | grab wire rope, ship unloader, failure analysis |
| Subjects: | T Technology > TD Environmental technology. Sanitary engineering > TD899.S68 Steam power plants T Technology > TS Manufactures > TS174 Maintainability (Engineering) . Reliability (Engineering) |
| Divisions: | Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis |
| Depositing User: | Putranto Redhian Yoga |
| Date Deposited: | 07 Mar 2022 03:01 |
| Last Modified: | 03 Apr 2023 02:10 |
| URI: | http://repository.its.ac.id/id/eprint/62178 |
Actions (login required)
 |
View Item |