Pengaruh Variasi Sudut Groove Pengelasan Pada Low Carbon Steel ASTM A36 Menggunakan Las SMAW Dengan Elektrode E6013 Terhadap Distorsi Dan Lebar HAZ.

Kusen, Muhamad Taufiqi (2019) Pengaruh Variasi Sudut Groove Pengelasan Pada Low Carbon Steel ASTM A36 Menggunakan Las SMAW Dengan Elektrode E6013 Terhadap Distorsi Dan Lebar HAZ. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10211500000109-Non_Degree.pdf]
Preview
Text
10211500000109-Non_Degree.pdf

Download (6MB) | Preview

Abstract

Teknologi pengelasan merupakan suatu teknologi yang sering digunakan dalam proses manufaktur, baik secara onshore, offshore, dan bidang konstruksi. Salah satu pengelasan yang sering digunakan adalah SMAW. teknik pengelasan menimbulkan efek merugikan, yaitu distorsi, Sehingga pengetahuan mengenai teknologi pengelasan sangat diperlukan untuk mencapai kesesuaian proses pengelasan agar diperoleh hasil yang optimal.
Dalam penelitian ini, pengelasan yang digunakan adalah las SMAW. Salah Satu yang perlu dikaji adalah distorsi pada pengelasan karena pengaruh dari variasi sudut groove 60, 65,dan 70 menggunakan elektrode E6013 material ASTM A 36 tebal 11 mm. Selanjutnya untuk mengetahui hasil sambungan dari ketiga variasi groove dengan mengamati sudut deformasi dan struktur makro.
Dari hasil pengujian yang dilakukan pada pengelasan SMAW baja ASTM A 36 dengan besar sudut groove 60,65,70 menghasilkan nilai distorsi arah transversal 1.082°, 1.846°, 2.331°. arah longitudinal 0,001134 mm, 0,00427 mm, 0.00639 mm. Pada hasil penelitian uji makro etsa rata-rata umum lebar HAZ pada las dengan sudut Groove 60 yaitu 2,55 mm lebih kecil dari sudut 65 yaitu 2,77 mm, dan sudut 70 yaitu 2,83 mm. Sehingga pada pengujian ini didapatkan semakin kecil sudut groove semakin sempit lebar HAZ.
================================================================================================
Welding technology is a technology that is often used in manufacturing processes, both onshore, offshore, and construction. One of the welding that is often used is SMAW. welding techniques cause adverse effects, namely distortion, so that knowledge of welding technology is needed to achieve the suitability of the welding process in order to obtain optimal results.
In this research report the welding used is SMAW welding. One of the things that needs to be studied is the distortion in welding due to the influence of variations in groove angles of 60, 65, and 70 using E6013 electrode ASTM A 36 11 mm thick material. Next to find out the results of the connection of the three groove variations by observing the deformation angle and macro structure.
From the results of testing carried out on the welding of SMAW ASTM A 36 steel with a large groove angle of 60 °, 65 °, 70 °, the value of the transverse direction distortion is 1,082 °, 1,846 °, 2,331 °. longitudinal direction 0.001134 mm, 0.00427 mm, 0.00639 mm. The results of the macro test etch the general average width of HAZ in the weld with Groove angle of 60 ° which is 2.55 mm smaller than the angle of 65 ° which is 2.77 mm, and the angle of 70 ° is 2.83 mm. So that in this test, the smaller the groove angle the wider the HAZ is obtained

Item Type: Thesis (Undergraduate)
Additional Information: RSMI 671.52 Kus p-1 2019
Uncontrolled Keywords: IPTEK, Pengelasan, SMAW, Groove, Distorsi dan HAZ.
Subjects: T Technology > TS Manufactures > TS227 Welding.
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: Muhamad Taufiqi Kusen
Date Deposited: 12 Apr 2022 01:28
Last Modified: 12 Apr 2022 01:28
URI: http://repository.its.ac.id/id/eprint/62309

Actions (login required)

View Item View Item