Pengaruh Variasi Heat Input Terhadap Kekasaran Permukaan Dan Lebar Haz Proses Pemotongan Bahan Baja Karbon Rendah Ss400 Dengan Menggunakan Elektroda Gouging 3.2 Mm Metode Las Smaw

Yoga, Willy (2019) Pengaruh Variasi Heat Input Terhadap Kekasaran Permukaan Dan Lebar Haz Proses Pemotongan Bahan Baja Karbon Rendah Ss400 Dengan Menggunakan Elektroda Gouging 3.2 Mm Metode Las Smaw. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10211500000078-Non_Degree.pdf]
Preview
Text
10211500000078-Non_Degree.pdf

Download (5MB) | Preview

Abstract

Pemotongan dalam dunia pengelasan saat ini sangat banyak digunakan. pada pengerjaan konstruksi pada baja ataupun konstruksi pada mesin untuk menghemat biaya dan waktu proses pemotongan bisa menggunakan elektroda gouging. Dalam proses pemotongan menggunakan elektroda gouging ini untuk mendapatkan hasil potongan yang baik dapat ditinjau sesuai dengan parameter pemotongan.
Pada penelitian ini, perlakuan yang diberikan adalah pemotongan dengan variasi arus yang berbeda yaitu 150 amphere, 165 amphere, 180 amphere. Pemotongan dilakukan dengan metode SWAW (Shield Metal Arc Welding) pada bahan plat baja karbon rendah SS400 dengan elektroda gouging diameter 3.2 mm . Kemudian diuji menggunkan uji makro etsa dan uji kekasaran permukaan.
Dari hasil penelitian didapatkan lebar haz yang paling sempit pada heat input 6041.958 J/mm (arus 180 A) dan nilai haz yang paling lebar terdapat pada heat input sebesar 6629.834 J/mm (arus 150A) dan nilai kekasaran Permukaan yang paling halus terdapat pada 6629.834 J/mm (150A).
================================================================================================
Cutting in the world of welding current is very widely used. on the construction work on steel or construction on the machine to save cost and time of cutting process can use electrodes gouging. In the process of cutting using this gouging electrode to get the pieces that can be reviewed, namely in accordance with the parameters of the cutting.
In this research, the variable that used in this research is difference electrical current used on SMAW (Shield Metal Arc Welding) cutting process. The electrical current variations are 150 amphere, 165 amphere, 180 amphere. The cutting is done on low carbon steel material with gouging electrodes 3.2 mm diameter, then tested using macro etching and surface roughness.
Of research results obtained by the most narrow haz width on heat input 6041,958 J/mm (the current 180 A) and the values of the most there are wide haz on heat input of 6,629,834 J/mm (current of 150A) and Surface Roughness test results the most subtle is present on 6,629,834 J/mm (150A).

Item Type: Thesis (Undergraduate)
Additional Information: RSMI 671.52 Yog p-1 2018
Uncontrolled Keywords: Pemotongan, elektroda gouging, SMAW, variasi arus, , makro etsa, kekasaran permukaan, Cutting, gouging electrode, SMAW, current variation, Metallography, Roughness
Subjects: T Technology > TS Manufactures > TS227 Welding.
Divisions: Faculty of Vocational > Mechanical Industrial Engineering
Depositing User: WILLY YOGA
Date Deposited: 13 Apr 2022 02:46
Last Modified: 13 Apr 2022 02:46
URI: http://repository.its.ac.id/id/eprint/62337

Actions (login required)

View Item View Item