Pengaruh Pelarut Isopropanol dan n-Butanol terhadap Penyatuan TiO2 dan H-ZSM-5 Hirarki dalam Komposit TiO2/H-ZSM-5 Hirarki Termodifikasi Karbon

Pramesti, Febrilia Agar (2019) Pengaruh Pelarut Isopropanol dan n-Butanol terhadap Penyatuan TiO2 dan H-ZSM-5 Hirarki dalam Komposit TiO2/H-ZSM-5 Hirarki Termodifikasi Karbon. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 01211540000021_Undergraduate_Theses.pdf]
Preview
Text
01211540000021_Undergraduate_Theses.pdf

Download (2MB) | Preview

Abstract

H-ZSM-5 hirarki telah berhasil disintesis dari ZSM-5 komersial dengan metode destruktif. H-ZSM-5 hirarki dikarakterisasi dengan BET, XRD, FTIR, dan SEM. Komposit TiO2/H-ZSM-5 hirarki termodifikasi karbon telah disintesis dengan metode sol gel dengan pelarut isopropanol dan n-butanol. Sampel hasil sintesis dikarakterisasi dengan XRD, FTIR, dan SEM. Hasil karakterisasi menunjukkan adanya agregat TiO2 pada sampel yang disintesis dengan n-butanol, sedangkan sampel yang disintesis dengan pelarut isopropanol tidak ditemukan adanya agregat. Tidak adanya agregat menunjukkan bahwa isopropanol adalah pelarut yang dapat membentuk komposit TiO2/H-ZSM-5 hirarki termodifikasi karbon dengan baik. Perbedaan kepolaran pelarut berpengaruh terhadap penyatuan TiO2 dan H-ZSM-5 hirarki.
================================================================================================
H-ZSM-5 hierarchy has been synthesized from commercial ZSM-5 by destructive method. H-ZSM-5 hierarchy is characterized by BET, XRD, FTIR, and SEM. Carbon modified TiO2/H-ZSM-5 hierarchy composites have been synthesized by sol-gel method with isopropanol and n-butanol as solvent. Synthesized composites were characterized by XRD, FTIR, and SEM. The characterization result showed the presence of TiO2 aggregates in composite synthesized with n-butanol, whereas agregat TiO2 was not found in composite synthesized with isopropanol. The absence of aggregate shows that isopropanol is a solvent that can form a good carbon modified TiO2/H-ZSM-5 hierarchy composite. The difference in solvent polarity affected the unification of TiO2 and H-ZSM-5 hierarchy.

Item Type: Thesis (Undergraduate)
Additional Information: RSKi 547 Pra p-1 2019
Uncontrolled Keywords: Komposit, ZSM-5, hirarki, TiO2, n-butanol, isopropanol, sol-gel
Subjects: Q Science > QD Chemistry
Q Science > QD Chemistry > QD716 Photocatalysis.
Divisions: Faculty of Mathematics and Science > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Febrilia Agar Pramesti
Date Deposited: 23 May 2022 02:39
Last Modified: 23 May 2022 02:39
URI: http://repository.its.ac.id/id/eprint/62787

Actions (login required)

View Item View Item