Pengaruh penambahan garam [NaCl] pada pertumbuhan nanopartikel TiO2 rutile dari prekurson TiCl3

Budiarti, Herny Ariesta (2014) Pengaruh penambahan garam [NaCl] pada pertumbuhan nanopartikel TiO2 rutile dari prekurson TiCl3. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2410100093-Undergraduate_Theses.pdf - Published Version

Download (4MB)

Abstract

Telah dilakukan sintesis nanopartikel TiO2 rutile dari prekursor TiCl3 menggunakan metode co-precipitation dengan variasi fraksi penambahan NaCl sebesar 0,83, 0,91, dan 0,94. Kemudian endapan dikalsinasi pada temperatur 600°C, 800°C, dan 1000°C selama 5 jam. Setelah diperoleh serbuk TiO2 kemudian sampel dikarakterisasi menggunakan, XRD, SEM, DSC/TGA, dan BET. Hasil karakterisasi XRD menunjukkan bahwa penambahan NaCl menghasilkan perpaduan fase rutile, anatase, brookite, dan Ti3O5. Ukuran partikel dan fraksi rutile paling besar diperoleh pada fraksi NaCl 0,83 dengan temperatur kalsinasi 1000°C yaitu sebesar 96,72 nm dengan fraksi rutile sebesar 0,87. Berdasarkan hasil karakterisasi DSC/TGA transformasi menjadi fase rutile terjadi pada temperatur ~800°C. Sedangkan hasil karakterisasi SEM menunjukkan bahwa, pengaruh penambahan NaCl pada suasana basa terhadap morfologi TiO2 tidak terlalu signifikan. Akan tetapi, semakin tinggi temperatur kalsinasi aglomerasi yang terjadi semakin besar. Dari hasil karakterisasi BET menunjukkan bahwa, penambahan NaCl menyebabkan luas permukaan partikel lebih kecil, akan tetapi diameter pori yang dihasilkan lebih besar. Penambahan NaCl paling optimal diperoleh pada fraksi NaCl 0,91 dengan energi aktivasi sebesar 9,20 kJ/mol. ========== Nanoparticle rutile TiO2 has been synthesized by co-precipitation method with salt addition. The NaCl fraction studied ware 0.83, 0.91, and 0.94. The solution was calcined at 600°C, 800°C, and 1000°C for 5 hours. The obtained TiO2 powder was characterized by XRD, SEM, DSC/TGA, and BET. The XRD result shows that salt addition produces the mixtures of rutile, anatase, brookite, and Ti3O5. The maximum particle size and fraction of rutile obtained were 96.720 nm and 0.87, respectively, for fraction of NaCl of 0.83 at 1000°C. Based on the DCS/TGA characterization, the anatase-to-rutile transformation was occured at ~800°C. In general, the morphology of TiO2 as observed through SEM does not change considerably by addition of NaCl. However, for higher calcination temperatures the particle agglomeration became bigger. The significant effect of NaCl addition is the reduction of surface area and the increase in pore diameter. From these result it was found that the maximum allowable of NaCl addition is 0.91 fraction whose energy activation being the lowest among other studied fractions, i.e. 9.20 kJ/mol.

Item Type: Thesis (Undergraduate)
Additional Information: RSF 620.5 Bud p
Uncontrolled Keywords: TiO2 rutile, TiCl3, NaCl, transformasi fase, coprecipitation, rutile TiO2, TiCl3, NaCl, phase transformation, copecipitation
Subjects: Q Science > QD Chemistry > QD553 Electrochemistry. Electrolysis
Divisions: Faculty of Industrial Technology > Physics Engineering > (S1) Undergraduate Theses
Depositing User: - Davi Wah
Date Deposited: 15 May 2019 04:19
Last Modified: 15 May 2019 04:19
URI: http://repository.its.ac.id/id/eprint/63031

Actions (login required)

View Item View Item