Pengeringan Sol Silika Dan Slurry ZnO Dengan Metode Spray Dryer Serta Aplikasi Flame Dalam Pengeringan Sol Silika

Zaman, M.Rizaldi and Kharisma, M. Saiful Rizal (2014) Pengeringan Sol Silika Dan Slurry ZnO Dengan Metode Spray Dryer Serta Aplikasi Flame Dalam Pengeringan Sol Silika. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
2310100054_2310100087-Undergraduate_Theses.pdf - Published Version

Download (3MB)
[img] Text
2310100054_2310100087_PUBLIKASI_S1_ITS_TEKNIK.pdf - Published Version

Download (1MB)
[img] Text
2310100054_2310100087_PRESENTATION.pdf - Published Version

Download (18MB)

Abstract

Spray drying banyak diaplikasikan di bidang industri untuk mengeringkan material karena memiliki berbagai keuntungan diantaranya mampu menghasilkan partikel hingga ukuran nanometer, proses kontinyu, kemurnian serta kristalinitas produk yang tinggi.Pada penelitian ini mencoba menggunakan Flame Spray Drying untuk mengeringkan partikel. Model yang digunakan pada penelitian ini adalah Sol Silika dan Slurry ZnO. Peralatan utama yang digunakan pada eksperimen berupa ultrasonic nebulizer, burner serta electrostatic precipitator. Analisa SEM (Scanning Electromagnetic Microscope) , XRD (XRay Diffraction) dan BET (Brunaur-Emmet-Teller) dilakukan untuk mengetahui morfologi, kristalinitas, ukuran dan juga luas permukaan dari partikel yang telah diperoleh. Morfologi dari silika sendiri berbentuk bulat kecil. Silika memiliki struktur amorf sehingga silika dapat digunakan sebagai material komposit karena tidak mempengaruhi material utama. Dari penelitian ini dapat disimpulkan bahwa untuk Slurry ZnO, semakin tinggi pH maka semakin besar ukuran kristal partikel, semakin tinggi tekanan maka semakin besar ukuran kristal partikel, dan morfologi dari ZnO berbentuk seperti jarum. ========== Spray drying widely applied in industry for drying the material because it has many advantages including particles capable of producing up to nanometer size, a continuous process, product purity and high crystallinity. In this study tries to use Flame Spray Drying to dry particles. The model used in this study is Sol Silica and Slurry ZnO.Major equipment used in this experiment are an ultrasonic nebulizer, burners and electrostatic precipitators. Analysis of SEM (Scanning Electromagnetic Microscope), XRD (X-Ray Diffraction) and BET (Brunaur- Emmett-Teller) was conducted to determine the morphology, crystallinity, size and surface area of the particles that have been obtained. Morphology of silica is small spherical. Silica has an amorphous structure that silica can be used as a composite material because it does not affect the main material. From this study it can be concluded that for ZnO slurry, the higher the pH, the greater the size of the crystal particles, the higher the pressure, the greater the size of the crystal particles, and the morphology of needle-shaped ZnO

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Spray dryingFlame spray drying,Silika,ZnO, Spray Drying, Flame spray drying,Silica
Subjects: Q Science > QC Physics > QC585.75.S55 Silica
Divisions: Faculty of Industrial Technology > Chemical Engineering > (S1) Undergraduate Theses
Depositing User: - Davi Wah
Date Deposited: 21 May 2019 05:00
Last Modified: 21 May 2019 05:00
URI: http://repository.its.ac.id/id/eprint/63051