Analisis Pengaruh Variasi pH dan Waktu Perendaman Terhadap Ketahanan Sweet Corrosion pada Baja ASTM A36 di Lingkungan Laut

Chakim, M.Charis (2019) Analisis Pengaruh Variasi pH dan Waktu Perendaman Terhadap Ketahanan Sweet Corrosion pada Baja ASTM A36 di Lingkungan Laut. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

Text 04311540000024-Undergraduate_Theses.pdf Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Perkembangan teknologi pada bidang kemaritiman terus dilakukan terutama pada bidang
transportasi dan konstruksi bangunan laut. Baja A36 merupakan baja yang sering
digunakan untuk bahan utama pada konstruksi bangunan laut. Dalam penggunaannya,
baja memiliki berbagai permasalahan, salah satunya adalah korosi yang dapat membuat
kegagalan suatu struktur. Salah satu penyebab korosi di laut yaitu terkandungnya gas CO2
dalam air laut. CO2 yang terlarut akan memicu terjadinya korosi yang biasa disebut sweet
corrosion. Tingginya tingkat CO2 di lingkungan laut disebabkan oleh meningkatnya
penggunaan bahan bakar fosil yang berakhir di laut. Tujuan dari penelitian ini adalah
untuk mengetahui ketahanan baja A36 terhadap sweet corrosion dan korosi yang di
timbulkannya secara makro dan mikro di lingkungan laut. Penelitian ini menggunakan
metode immersion corrosion test dengan menggunakan metode perhitungan weight loss.
Parameter yang digunakan adalah pH 4, pH 5, pH 6, dan pH 7 dan waktu perendaman
24 jam,72 jam,120 jam, dan 168 jam. Hasil penelitian menunjukkan bahwa ketahanan
relatif dari baja ASTM A36 terhadap sweet corrosion adalah baik. Selain itu didapatkan
persamaan regresi untuk memprediksi laju korosi akibat CO2 untuk pH 4, 5, 6 dan 7
adalah y = 0.05x + 9.08, y = -2.03x + 13.47, y = -3.57x + 21.59, dan y = -2.72x + 17.14.
Hasil pengamatan pada permukaan logam secara makro maupun mikro terlihat bahwa
hasil korosi yang dihasilkan adalah localized corrosion dan general corrosion.
=========================================================
Technological developments in the maritime field will always carried out especially in
sea transportation and sea building construction. ASTM A36 is a steel commonly used
for the main material in marine building construction. In its use, steel has various
problems, one of which is corrosion can make a structure fail. One of the causes of
corrosion in the sea is the presence of CO2 gas in seawater. Dissolved CO2 will trigger
corrosion is usually called sweet corrosion. The high level of CO2 in the marine
environment is cause by the increasing use of fossil fuels that are heading towards the
sea. The purpose of this study was to determine the resistance of ASTM A36 against
sweet corrosion and corrosion caused form by macro and micro in the marine
environment. This study uses the immersion corrosion test method by calculate based on
the weight loss. The parameters used were pH 4, pH 5, pH 6, and pH 7 and the immersion
time used was 24 hours, 72 hours, 120 hours, and 168 hours. The result show if the
corrosion relative resistance of ASTM A36 steel on sweet corrosion environtment is good.
Beside of that derivative regression equation for predict corrosion rate caused CO2, and
the equation for pH 4, 5, 6 dan 7 is y = 0.05x + 9.08, y = -2.03x + 13.47, y = -3.57x +
21.59, y = -2.72x + 17.14. Then, the result of observing on steel surface use macro and
micro observation technique showed the corrosion form is localized corrosion and general
corrosion.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Baja A36, Korosi CO2, Immersion corrosion test, pH, Sweet corrosion.
Subjects:	T Technology > TC Hydraulic engineering. Ocean engineering > TC1665 Offshore structures--Materials.
Divisions:	Faculty of Marine Technology (MARTECH) > Ocean Engineering > 38201-(S1) Undergraduate Thesis
Depositing User:	Chakim M. Charis
Date Deposited:	04 Jun 2026 04:09
Last Modified:	04 Jun 2026 04:09
URI:	http://repository.its.ac.id/id/eprint/63501