Rancang Bangun Reaktor Fotokatalisis untuk Mengukur Fotodegradasi Methylene Blue secara Real Time dengan TiO2 yang Dilapiskan pada Kain Cotton Sifon

Mijayanti, Tika (2019) Rancang Bangun Reaktor Fotokatalisis untuk Mengukur Fotodegradasi Methylene Blue secara Real Time dengan TiO2 yang Dilapiskan pada Kain Cotton Sifon. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 01111540000051-Undergraduate_Thesis.pdf Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Penelitian ini bertujuan merancang reaktor fotokatalisis yang mampu mengukur fotodegradasi secara real time, memahami proses pembuatan substrat TiO2 pada serat kain, mengetahui pengaruh jenis kain sebagai substrat dalam degradasi larutan Methylene Blue, dan mengetahui hasil tegangan yang didapatkan dari pengukuran. Proses pembuatan katalis TiO2 pada substrat kain yaitu dengan mencampur TiO2 dengan resin dan perekat dengan perbandingan massa 3,5 gr : 7gr : 2,33 gr lalu di aduk dengan stirrer selama 1 jam. Kemudian dilapiskan pada kain. Jenis kain yang digunakan adalah kain baby terry dan kain cotton sifon. Hasil yang diperoleh penelitian ini adalah nilai absorbansi dan nilai tegangan. Telah berhasil dirancang dan dibuat reaktor fotokatalisis menggunakan sensor photodioda mampu mengukur fotodegradasi secara real time 0-5ppm dengan output photodioda 100-500mV. Berhasil membuat substrat TiO2 yang dicampurkan dengan resin lalu dilapiskan ke kain cotton sifon dan baby terry. TiO2 yang dilapiskan kain cotton sifon dapat mendegradasi Methylene blue lebih baik dibandingkan kain baby terry dilihat dari hasil nilai absorbansi.
===================================================================================================================================
This research aims to design a photocatalyst reactor capable of measuring photodegradation in real time, understanding the process of making TiO2 substrate on fabric fibers, knowing the effect of the type of fabric as a substrate in the degradation of Methylene blue solution, and knowing the results of the stress obtained from measurements. The process of making TiO2 catalyst on fabric substrate is by mixing TiO2 with resin and adhesive with a mass ratio of 3.5 gr: 7gr: 2.33 gr then in the stirrer for a hour. then coated on cloth. The type of fabric used is baby terry and cotton chiffon. The results obtained in this study are absorbance values and voltage values. The photocatalytic reactor has been successfully designed and made using a photodiode sensor capable of measuring photodegradation in real time from 0 to 5 ppm with a photodiode output of 100-500 mV. Successfully made TiO2 substrate mixed with resin and then coated onto cotton chiffon and baby terry cloth. TiO2 coating with cotton chiffon fabric can degrade Methylene blue better than baby terry fabric seen from the absorbance value.

Item Type:	Thesis (Other)
Additional Information:	RSF 541.395 Mij r-1 2019
Uncontrolled Keywords:	TiO2, degradasi, baby terry, cotton sifon, absorbansi
Subjects:	Q Science Q Science > QC Physics Q Science > QC Physics > QC100.5 Measuring instruments (General)
Divisions:	Faculty of Natural Science > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Tika Mijayanti
Date Deposited:	20 Jul 2026 03:02
Last Modified:	20 Jul 2026 03:02
URI:	http://repository.its.ac.id/id/eprint/64342

Actions (login required)

View Item