Analisis Pengaruh Penambahan Energizer Na2CO3 pada Proses Carburizing dengan Variasi Waktu Tahan Terhadap Kekerasan dan Struktur Mikro Baja Karbon Medium

Dewantara, AM Bayu (2019) Analisis Pengaruh Penambahan Energizer Na2CO3 pada Proses Carburizing dengan Variasi Waktu Tahan Terhadap Kekerasan dan Struktur Mikro Baja Karbon Medium. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511540000075_Undergraduate_Theses.pdf - Accepted Version Restricted to Repository staff only Download (8MB) | Request a copy

Abstract

Ditemui suatu kegagalan material pada poros mesin uap penggilingan di Pabrik Gula Gending. Setelah dilakukan uji komposisi, diketahui material gagal tesebut adalah baja karbon medium dengan unsur karbon sebesar 0,4 %. Nilai kekerasan baja karbon medium tersebut berkisar diantara 170 – 210 HV, sedangkan poros adalah bagian yang memerlukan ketahanan aus yang tinggi dengan kekerasan permukaan sebesar 310 HV. Maka dari itu dilakukan pack carburizing dengan metode direct quench terhadap baja karbon medium. Proses karburisasi dilakukan pada temperatur 930 ºC, dengan variasi komposisi penambahan energizer Na2CO3 0, 10, 20, 30 %berat, dan variasi waktu tahan selama 1 dan 3 jam. Hasil pengujian metalografi menunjukkan karburisasi dengan waktu tahan 3 jam memiliki fasa retained austenite yang lebih banyak pada permukaan apabila dibandingkan dengan waktu tahan 1 jam, dan dapat ditemui juga nilai kekerasan permukaan spesimen 0%En-Na2CO3_Ht3, 10%En-Na2CO3_Ht3, 20%En-Na2CO3_Ht3, 30%En-Na2CO3_Ht3 yang lebih tinggi dibandingkan dengan spesimen 0%En-Na2CO3_Ht1, 10%En-Na2CO3_Ht1, 20%En-Na2CO3_Ht1, 30%En-Na2CO3_Ht1, yakni 808.4, 646.2, 597, 575.4 HV untuk waktu tahan 3 jam, dan 781.4, 621.6, 590, 546.4 HV untuk waktu tahan 1 jam. Begitu pula dengan kedalaman lapisan yang didapatkan, dengan waktu tahan 3 jam, kedalaman lapisan yang didapat lebih dalam apabila dibandingkan dengan waktu tahan 1 jam. Sedangkan untuk penambahan komposisi energizer, kedalaman lapisan yang dihasilkan menurun, dan memiliki nilai kekerasan permukaan yang juga menurun. Sehingga dianggap keefektifitasan energizer Na2CO3 pada proses pack carburization terhadap baja karbon medium terdapat pada penambahan kurang dari 10%
====================================================================================================================================
A material failure was encountered on the steam milling machine shaft at the Gending Sugar Factory. After testing the composition, it is known that the failed material is medium carbon steel with a carbon element of 0.4%. The hardness value of the medium carbon steel ranges from 170-210 HV, while the shaft is a part that requires high wear resistance with a surface hardness of 310 HV. Pack carburizing is done by direct quench method on medium carbon steel. The carburization process was carried out at a temperature of 930 ºC, with variations in the composition of the addition of Na2CO3 energizer 0, 10, 20, 30 %w, and the variation of holding time for 1 and 3 hours. Metallographic test results show that carburization with a hold time of 3 hours have more retained austenite phase on the surface compared to a 1 hour hold time, and can also be found for higher values of specimen surface hardness 0%En-Na2CO3_Ht3, 10%En-Na2CO3_Ht3, 20%En-Na2CO3_Ht3, 30%En-Na2CO3_Ht3 compared to specimen 0%En-Na2CO3_Ht1, 10%En-Na2CO3_Ht1, 20%En-Na2CO3_Ht1, 30%En-Na2CO3_Ht1, which are 808.4, 646.2, 597, 575.4 HV for a 3 hour hold time, and 781.4, 621.6, 590, 546.4 HV for 1 hour holding time. Likewise with the depth of case that obtained, with a hold time of 3 hours, the depth of the case obtained deeper when compared to hold time of 1 hour. As for the addition of the energizer composition, the depth of case descending, and has a value of surface hardness that decrease as well. The effectiveness of the Na2CO3 energizer in the pack carburization process on medium carbon steel is found in additions of less than 10%

Item Type:	Thesis (Other)
Additional Information:	RSMt 671.36 Dew a-1 2019 3100019081440
Uncontrolled Keywords:	Difusi, Energizer, Karburisasi, Kedalaman Lapisan, Kekerasan, Poros
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	AM Bayu Dewantara
Date Deposited:	12 Nov 2025 10:06
Last Modified:	12 Nov 2025 10:06
URI:	http://repository.its.ac.id/id/eprint/64738